The invention relates to a high performance fireproof building materials brick, the preparation method is as follows: (1) preparation of fireproof filler, by weight, 5 - 20, dipentaerythritol N P composite flame retardant 20 - 30, 21 - 27, pearl sand perlite 10 - 15, wet mica 10 - 18, 26 - 38, epoxy resin 16 - 28 acicular wollastonite powder mixing, be fireproof filler; (2) building materials brick fire brick surface in slotting, cutting fire groove, a square structure in fire tank, fire brick surface is evenly distributed (3 6*6 matrix;) is filled with fireproof filler in the internal surface of the fireproof slot building materials brick, fire clay fill after plugging, plugging after nature dry. The fireproof property of the building material bricks obtained by the invention is excellent.
【技术实现步骤摘要】
一种具有高防火性能的建筑材料砖
本专利技术涉及一种填料，特别涉及一种具有高防火性能的建筑材料砖。
技术介绍
近年来随着建筑行业的飞速发展，火灾的防控也面临巨大的挑战，防火的重要性不言而喻，防火填料作为有效的防火材料，可以对火势进行有效的阻燃，防止进一步蔓延，可以有效的减少火灾对人民生命和财产造成的威胁。
技术实现思路
本专利技术针对上述问题提出了一种具有高防火性能的建筑材料砖。具体的技术方案如下：一种具有高防火性能的建筑材料砖，其特征在于，制备方法如下：（1）制备防火填料，按重量份数计，双季戊四醇5—20份、N-P复合阻燃剂20—30份、珍珠砂21—27份、膨胀珍珠岩10—15份、湿法云母粉10—18份、环氧树脂26—38份、针状硅灰石粉16—28份进行搅拌混合，得到防火填料；（2）建筑材料砖开槽，在防火砖表面切割防火槽，防火槽呈方形结构，在防火砖表面呈6*6矩阵均匀分布；（3）在建筑材料砖表面的防火槽内部填充防火填料，填充完毕后使用防火泥封堵，封堵后自然晾干即可。上述一种具有高防火性能的建筑材料砖，其特征在于，所述N-P复合阻燃剂为S-N-P复合型阻燃剂与MH复合N...
【技术保护点】
一种具有高防火性能的建筑材料砖，其特征在于，制备方法如下：（1）制备防火填料，按重量份数计，双季戊四醇5—20份、N‑P复合阻燃剂20—30份、珍珠砂21—27份、膨胀珍珠岩10—15份、湿法云母粉10—18份、环氧树脂26—38份、针状硅灰石粉16—28份进行搅拌混合，得到防火填料；（2）建筑材料砖开槽，在防火砖表面切割防火槽，防火槽呈方形结构，在防火砖表面呈6*6矩阵均匀分布；（3）在建筑材料砖表面的防火槽内部填充防火填料，填充完毕后使用防火泥封堵，封堵后自然晾干即可。
【技术特征摘要】
1.一种具有高防火性能的建筑材料砖，其特征在于，制备方法如下：（1）制备防火填料，按重量份数计，双季戊四醇5—20份、N-P复合阻燃剂20—30份、珍珠砂21—27份、膨胀珍珠岩10—15份、湿法云母粉10—18份、环氧树脂26—38份、针状硅灰石粉16—28份进行搅拌混合，得到防火填料；（2）建筑材料砖开槽，...
【专利技术属性】
技术研发人员：徐鹏，
申请(专利权)人：镇江市太浪新材料科技有限公司，
类型：发明
国别省市：江苏,32