The invention discloses a burning stick can prevent legitimate resistance with bottom rubber rain boots, calculated according to the weight, including 80 styrene butadiene rubber and nitrile butadiene rubber, chloroprene rubber, 20 1.5 0.4 0.5, sulfur accelerator M 0.1 0.2, Zinc Oxide 5, Magnesium Oxide 4, stearic acid 1.5, antioxidant D 1.5 2.5, calcium carbonate 10 20, 5, two pine tar butyl 15, 5, 40 carbon black ointment and semi reinforcing black antiscorching agent YG 10, 1, 0.4 and 0.2 antiscorcher PVI 0.1 0.5. The large base adhesive produced by this formula has good oil resistance and low cost, and it can adapt to the operation environment of contact oil, suitable for oil operation protection, and it is not easy to scorch, and can greatly improve the safety of rubber processing.
【技术实现步骤摘要】
一种能防止焦烧的贴合法耐油靴用大底胶
本专利技术涉及胶鞋制造领域，涉及靴用大底胶配方，尤其涉及一种能防止焦烧的贴合法耐油靴用大底胶。
技术介绍
普通橡胶材料制成的鞋子，其大底胶通常为天然橡胶加上合成橡胶，使用范围广、成本低，但由于天然橡胶与油液介质溶解度参数不够悬殊，造成大底胶耐油性较差，因此，常用的大底胶配方并不能用于接触油类的防护用靴。焦烧是一种胶料早期硫化现象，产生焦烧的原因有：配合不当，如硫化剂、促进剂用量太多；操作不当，如辊温过高、过早加入硫黄、或加入硫化剂后混炼时间太长。混炼不均造成硫化剂和促进剂局部集中；胶料冷却停放不当。如停放过久，停放场地温度过高或空气流通等，出现焦烧现象时，胶料表面不光滑，麻面可塑度降低，严重时胶料表面会出现大小不等的颗粒。由于夏季气温较高，容易造成耐油靴用鞋面胶在混炼机加工时发生焦烧现象，造成胶料报废。
技术实现思路
本专利技术的目的是针对现有技术的不足，而提供一种能防止焦烧的贴合法耐油靴用大底胶，用该配方生产的大底胶其耐油性能较好，成本较低，能适应耐油的操作环境，适用于耐油作业的防护，且加工过程不易发生焦烧现象，能大幅提高胶料加工的安全性。实现本专利技术目的的技术方案是：一种能防止焦烧的贴合法耐油靴用大底胶，按照重量份计算，包括丁苯橡胶80、丁腈橡胶20、氯丁橡胶1.5、硫磺0.4-0.5、促进剂M0.1-0.2、氧化锌5、氧化镁4、硬脂酸1.5、防老剂D1.5-2.5、碳酸钙10-20、松焦油5、二丁酯15、黑油膏5、炭黑40、半补强炭黑10、防焦剂YG-10.2-0.4、防焦剂PVI0.1-0.5。本专利技术的优点在...
【技术保护点】
一种能防止焦烧的贴合法耐油靴用大底胶，按照重量份计算，包括：丁苯橡胶80、丁腈橡胶20、氯丁橡胶1.5、硫磺0.4‑0.5、促进剂M 0.1‑0.2、氧化锌5、氧化镁4、硬脂酸1.5、防老剂D 1.5‑2.5、碳酸钙 10‑20、松焦油5、二丁酯15、黑油膏5、炭黑40、半补强炭黑10、防焦剂YG‑1 0.2‑0.4、防焦剂PVI 0.1‑0.5。
【技术特征摘要】
1.一种能防止焦烧的贴合法耐油靴用大底胶，按照重量份计算，包括：丁苯橡胶80、丁腈橡胶20、氯丁橡胶1.5、硫磺0.4-0.5、促进剂M0.1-0.2、氧化锌5、氧化镁4、硬脂酸1.5、防老剂D1.5-2.5、碳酸钙10-20、松焦油5、二丁酯15、黑油膏5、炭黑40、半补强炭黑10、防焦剂YG-10.2-0.4、防焦剂PVI0.1-0...
【专利技术属性】
技术研发人员：杨军，
申请(专利权)人：桂林洁宇环保科技有限责任公司，
类型：发明
国别省市：广西,45