The invention discloses a biodegradable polypropylene composition and preparation method thereof, wherein the degradable polypropylene composite composition, including by compatibilizer weight polypropylene 20 30 copies, 60 copies, 40 starch grafted polypropylene 2 3 copies, 2 copies of the 0.3 coupling agent and blending. Compared with the prior art, the degradable polypropylene composite composition by starch and polypropylene blend of the invention, the prepared polypropylene composite composition can be degraded, and the compatibility and adding coupling agents grafted polypropylene, improve the compatibility of polypropylene and starch, can enhance the mechanical properties degradation of polypropylene composite composition.
【技术实现步骤摘要】
一种可降解聚丙烯复合组合物及其制备方法
本专利技术涉及食品塑料包装原料
，尤其涉及一种可降解聚丙烯复合组合物及其制备方法。
技术介绍
随着“白色污染”的日趋严重及人们环保意识的不断提高，可生物降解的环境友好材料越来越受到人们的青睐，淀粉由于其广泛的来源、低廉的价格被认为是最具发展前景的生物降解材料之一，使得淀粉改性聚丙烯的研究备受关注。然而，由于淀粉是一种强极性亲水性天然高分子，分子间及分子内都存在极强的氢键；而聚丙烯一般为疏水性高分子，极性很小，淀粉和聚丙烯的结构和极性相差很远，因而淀粉和聚丙烯的相容性差，严重阻碍了聚丙烯/淀粉复合材料的发展与应用。
技术实现思路
本专利技术的目的在于克服现有技术中的缺点和不足，提供一种可降解聚丙烯复合组合物及其制备方法。本专利技术是通过以下技术方案实现的，一种可降解聚丙烯复合组合物，包括按重量份的聚丙烯20-30份、淀粉40-60份、接枝聚丙烯的相容剂2-3份、偶联剂0.3-2份共混而成。相对于现有技术，本专利技术的可降解聚丙烯复合组合物通过淀粉和聚丙烯共混，制备得到可降解的聚丙烯复合组合物，且通过加入接枝聚丙烯的相容剂及偶...
【技术保护点】
一种可降解聚丙烯复合组合物，其特征在于：包括按重量份的聚丙烯20‑30份、淀粉40‑60份、接枝聚丙烯的相容剂2‑3份、偶联剂0.3‑2份共混而成。
【技术特征摘要】
1.一种可降解聚丙烯复合组合物，其特征在于：包括按重量份的聚丙烯20-30份、淀粉40-60份、接枝聚丙烯的相容剂2-3份、偶联剂0.3-2份共混而成。2.根据权利要求1所述的可降解聚丙烯复合组合物，其特征在于：所述相容剂为单硬脂醇甘油醚或单硬脂酸甘油酯中的一种或两种混合。3.根据权利要求1所述的可降解聚丙烯复合组合物，其特征在于：所述偶联剂为铝酸酯偶联剂或钛酸酯偶联剂。4.根据权利要求1-3中任一权利要求所述的可降解聚丙烯复合组合物，其特征在于：所述接枝聚丙烯的相容剂按重量比为所述淀粉的5％。5.根据权利要求4所述的可降解聚丙烯复合组合物，其特征在于：所述偶联剂按重量比为所述淀粉质量的1％-2％。6.一种可降解聚丙烯复合组合物的制备方法，其特征在于：包括以下步骤：(1)称取淀粉后，加入偶联剂，高速搅...