一种能形成大颗粒凸点的水性涂料及其制备方法技术

本发明专利技术公开了一种水性涂料及其制备方法，所述涂料含有凹凸棒石粘土和余量的丙烯酸类乳液。所述凹凸棒石粘土占涂料的重量份数为5~20wt%，优选10~20wt%，进一步优选15wt%。所述水性涂料的制备方法为：将凹凸棒石粘土于搅拌下加入丙烯酸类乳液中，搅拌，即可得到水性涂料。本发明专利技术所述水性涂料是一种有环保作用、可吸附有害气体，可在较脆材质上形成大颗粒凸点式涂层，且凸出点饱满结实的水性涂料。

A water-based coating which can form large particle bumps and its preparation method

The invention discloses a water-based coating and a preparation method, the coating contains attapulgite clay and residual acrylic emulsion. The weight portion of the attapulgite clay is 5~20wt%, and 10~20wt% is preferred, and 15wt% is further optimized. The preparation method of the water borne coating is as follows: the attapulgite clay is added into the acrylic emulsion and stirred, and the waterborne coating can be obtained. The waterborne coating is an environmentally friendly, adsorbable harmful gas, and can form large particle bump coating on the brittle material, and the convex point is full and strong.

【技术实现步骤摘要】
一种能形成大颗粒凸点的水性涂料及其制备方法
本专利技术属于涂料组合物领域，具体地说是涉及水性涂料组合物。
技术介绍
建筑涂料可分成两大类，有机涂料和无机涂料。目前有机水性涂料倍受青睐，这种涂料是水性涂料，没有或很少有有机溶剂，因此对人的身体危害、对环境污染都很小，使用时很方便，用水稀释，以水清洗。这种涂料与传统低质水性涂料不一样，在建筑物表面结成的膜不溶于水，耐污、耐擦、防水、耐候性好。对水性改性防水涂料的施工性来讲，最大的特点是夏天可厚涂，春秋可薄涂，冬天可掺加助剂施工，即施工前加在防水涂料内掺加2-3%的助剂，搅拌均匀后涂刷，这样做能保证低温施工质量。水性防水涂料的粘结力和成膜质量仍受施工气温高低的影响，气温越高，分散渗透性越强，粘结力越高，成膜质量越好；施工气温越低，涂膜质量就差。此外建筑涂料也在向功能性方向发展，其中有喷涂表面呈星点状凸出点的涂料，可吸附有害气体；但此类技术存在着喷涂凸出点很小或呈细丝状，涂料干燥后凸出点会收缩凹进，不饱满，或是凸出点易脱落等问题。同时为了满足人们多样化的需求，在制造墙面、吊顶等装饰板材的工艺中，经常对这些平面板材的表面进行各种处理，添加二维的本文档来自技高网...

【技术保护点】
一种水性涂料，其特征在于，所述涂料含有凹凸棒石粘土和余量的丙烯 酸类乳液。

【技术特征摘要】
1.一种水性涂料，其特征在于，所述涂料含有凹凸棒石粘土和余量的丙烯酸类乳液。2.如权利要求1所述的涂料，其特征在于，所述凹凸棒石粘土占涂料的重量份数为5~20wt%，优选10~20wt%，进一步优选15wt%。3.如权利要求1或2所述的涂料，其特征在于，所述凹凸棒石粘土的粒径为1~8mm，优选2~6mm，进一步优选3~5mm。4.如权利要求1-3之一所述的涂料，其特征在于，所述涂料的粘度为800~3500mPa·s，优选1200~3500mPa·s，进一步优选2000~3500mPa·s。5.一种如权利要求1-4之一所述水性涂料的制备方法，其特征在于，所述方法为：将凹凸棒石粘土于搅拌下加入丙烯酸类乳液中，搅拌，即可得到水性涂料。6.如...