一种环保无毒玩具材料及其制备工艺制造技术

本发明专利技术公开了一种环保无毒玩具材料及其制备工艺，玩具材料组分按重量份数包括聚丙烯20‑40份、矿物填料10‑20份、天然树脂8‑18份、碳酸钙5‑15份、聚乙烯10‑20份、纳米氧化硅6‑16份、季戊四醇4‑12份、石蜡6‑18份、硬脂酸钡8‑20份、硅微粉5‑12份、表面活性剂4‑10份，本发明专利技术制备工艺简单，制得的玩具材料环保无毒，还具有优异的柔韧性和拉伸强度，适合于制作玩具。

A kind of environmentally friendly and nontoxic toy material and its preparation technology

The invention discloses a non-toxic toy material and its preparation process, toy material components according to the weight of 20 40 copies, including polypropylene mineral filler 10 20 copies, 18 copies, 8 natural resin calcium carbonate 5 15 copies, 20 copies, 10 polyethylene nano silicon oxide 6 16 Ji Wu, 12, four alcohol 4 paraffin 6 18 copies, 20 copies of 8 barium stearate, silica powder 12, 5 surfactant 4 10 copies, the invention has simple preparation technology, environmental protection toy materials prepared non-toxic, also has the flexibility and excellent tensile strength, suitable for making toys.

【技术实现步骤摘要】
一种环保无毒玩具材料及其制备工艺
本专利技术涉及玩具材料制备
，具体为一种环保无毒玩具材料及其制备工艺。
技术介绍
随着玩具行业的发展，消费者对玩具的环保及安全性能越来越重视，要求也越来越高。特别是对于3岁以下婴幼儿来说，安全性能为重要，如耐咬力、撕裂力、拉/扭力，简称拉扭撕咬性能。因此，在制造儿童玩具时，对材料的选用也是越来越苛刻。目前常用的玩具材料为热塑性橡胶、热塑性弹等；而现有的玩具制作材料环保性能差，可降解性能差。
技术实现思路
本专利技术的目的在于提供一种环保无毒玩具材料及其制备工艺，以解决上述
技术介绍
中提出的问题。为实现上述目的，本专利技术提供如下技术方案：一种环保无毒玩具材料,玩具材料组分按重量份数包括聚丙烯20-40份、矿物填料10-20份、天然树脂8-18份、碳酸钙5-15份、聚乙烯10-20份、纳米氧化硅6-16份、季戊四醇4-12份、石蜡6-18份、硬脂酸钡8-20份、硅微粉5-12份、表面活性剂4-10份。优选的，玩具材料组分优选的成分配比包括聚丙烯30份、矿物填料15份、天然树脂13份、碳酸钙10份、聚乙烯15份、纳米氧化硅11份、季戊四醇8份、石蜡12份本文档来自技高网...

【技术保护点】
一种环保无毒玩具材料,其特征在于：玩具材料组分按重量份数包括聚丙烯20‑40份、矿物填料10‑20份、天然树脂8‑18份、碳酸钙5‑15份、聚乙烯10‑20份、纳米氧化硅6‑16份、季戊四醇4‑12份、石蜡6‑18份、硬脂酸钡8‑20份、硅微粉5‑12份、表面活性剂4‑10份。

【技术特征摘要】
1.一种环保无毒玩具材料,其特征在于：玩具材料组分按重量份数包括聚丙烯20-40份、矿物填料10-20份、天然树脂8-18份、碳酸钙5-15份、聚乙烯10-20份、纳米氧化硅6-16份、季戊四醇4-12份、石蜡6-18份、硬脂酸钡8-20份、硅微粉5-12份、表面活性剂4-10份。2.根据权利要求1所述的一种环保无毒玩具材料,其特征在于：玩具材料组分优选的成分配比包括聚丙烯30份、矿物填料15份、天然树脂13份、碳酸钙10份、聚乙烯15份、纳米氧化硅11份、季戊四醇8份、石蜡12份、硬脂酸钡14份、硅微...