一种电熔镁砂及其制备工艺制造技术

本发明专利技术提出了一种电熔镁砂及其制备工艺，解决了现有技术中传统电熔镁砂制备工艺设计不足进而造成含钙量低的问题，一种电熔镁砂，包含菱镁矿、白云石原料，且二者的重量比5.3∶1，在冶炼高钙电熔镁砂时，采用炉口加盖封闭方式，使熔炼过程中产生的烟气，集中进入烟气回收系统，烟气经除尘后进入中间储仓，最后引入二氧化碳回收系统，减少环境污染，节约能源。

A kind of electrofusion magnesia sand and its preparation process

The present invention provides a fused magnesia and its preparation process, solves the traditional fused magnesia preparation process design deficiencies causing low in calcium, a fused magnesia, magnesite and dolomite containing raw materials, and two of the weight ratio of 5.3 to 1, in the high calcium electric smelting magnesite, the mouth closed stamped, the flue gas generated in the process of smelting, concentrated into the flue gas recovery system, flue gas after the dust into the bin, finally the introduction of carbon dioxide recovery system, reduce environmental pollution, save energy.

【技术实现步骤摘要】
一种电熔镁砂及其制备工艺
本专利技术涉及冶炼行业
，特别是指一种电熔镁砂及其制备工艺。
技术介绍
传统电熔镁砂主要以氧化镁为主要成份，是一种纯度高、熔点高、结晶粒大、结构致密、抗渣性强、化学性能稳定的碱性镁质耐火材料，被广泛应用于制作高档镁砖、镁碳砖及不定形耐火材料。传统电熔镁砂凭借其优良的性能在普通钢包上具有良好的使用效果，而在精炼洁净钢的钢包上存在不足，如传统电熔镁砂氧化钙含量较低，不能有效吸收钢水中的杂质，不利于洁净钢的冶炼。且传统电熔镁砂在冶炼时，采用炉口敞开冶炼方式，生产过程中产生的废气直接排入大气，废气带走热量、粉尘和CO2，不仅污染环境而且造成能源和资源的浪费。因而，开发新一代高钙电熔镁砂及其制备工艺对洁净钢的冶炼和节约能源具有重要意义。
技术实现思路
本专利技术提出一种电熔镁砂及其制备工艺，解决了现有技术中传统电熔镁砂制备工艺设计不足进而造成含钙量低的问题。本专利技术的技术方案是这样实现的：一种电熔镁砂，包含菱镁矿、白云石原料，且二者的重量比5.3∶1。优选的，电熔镁砂内含MgO≥87.5％，CaO9～10％，SiO2≤1.0％，Fe2O3≤0.8％，Al2O3≤0本文档来自技高网...

【技术保护点】
一种电熔镁砂，其特征在于，包含菱镁矿、白云石原料，且二者的重量比5.3∶1。

【技术特征摘要】
1.一种电熔镁砂，其特征在于，包含菱镁矿、白云石原料，且二者的重量比5.3∶1。2.一种电熔镁砂，其特征在于：电熔镁砂内含MgO≥87.5％，CaO9～10％，SiO2≤1.0％，Fe2O3≤0.8％，Al2O3≤0.2％，体积密度大于3.35g/cm3。3.如权利要求1或2所述的一种电熔镁砂的制备工艺，其特征在于，包含以下步骤：1)开炉阶段：用矿石料铺底410mm高，电极下降，找到电极窝，用小块石墨料连接三电极窝，下降电极，...

【专利技术属性】
技术研发人员：王伟伟，刘丽，赵伟，任林，胡玲军，王次明，刘靖轩，刘洋，曹仁锋，张晓波，赵冉，于九利，
申请(专利权)人：北京利尔高温材料股份有限公司，
类型：发明
国别省市：北京,11