The invention discloses a process for manufacturing a flame retardant corrugated board, which comprises the following steps: preparing adhesive; adhesive paper; coatings; drying setting; cooling; pressure; longitudinal and transverse; flame retardant infiltration and drying; cut corrugated cardboard stacking, placed in the warehouse. Reasonable arrangements for the manufacturing process of the invention, the corrugated layer prepared between high bonding strength, stable performance, and has the advantages of flame retardant, safe and reliable, significant for improving safety of packaged goods, and has a broad market prospect in the popularization of flame retardant of packaging materials.
【技术实现步骤摘要】
一种阻燃瓦楞纸板的制造工艺
本专利技术涉及瓦楞纸板生产工艺，具体是一种阻燃瓦楞纸板的制造工艺。
技术介绍
瓦楞纸板是一个多层的复合结构，它最少由一层瓦楞形中间层及一层纸板构成。瓦楞纸板具有较高的机械强度，能吸收货物搬运过程中的碰撞和摔跌，主要用于制造纸箱、纸箱的夹心以及易碎商品的外包装。瓦楞纸板受温度影响小，遮光性能好，一般受湿度影响也较小，但防火性能不好，遇高温或明火易燃。日前，我国瓦楞纸板生产厂商的数目不断增加，其生产技术也得到了长足进步。但是，作为包装材料使用的瓦楞纸板在其使用过程中阻燃性能的缺失，会造成其包装的物品在储运过程中有火灾隐患，甚至会给人们带来一定的经济损失。
技术实现思路
本专利技术提供了一种阻燃瓦楞纸板的制造工艺，以解决上述技术问题。一种阻燃瓦楞纸板的制造工艺，包括如下步骤：(1)制胶：将水、淀粉、碱用、树酯胶粘剂、硼砂按比例混合充分搅拌成胶；(2)上粘胶裱纸：瓦楞原纸经过压楞后，由传递装置将其送入上胶机，涂上玉米淀粉粘合剂，人工挂上里纸，在上胶机裱合成瓦楞纸板；上胶机的涂胶辊表面镀铬，厚度为0.5mm，并经磨削加工；(3)覆层：将裱好的单层瓦楞...
【技术保护点】
一种阻燃瓦楞纸板的制造工艺，其特征在于，包括如下步骤：(1)制胶：将水、淀粉、碱用、树酯胶粘剂、硼砂按比例混合充分搅拌成胶；(2)上粘胶裱纸：瓦楞原纸经过压楞后，由传递装置将其送入上胶机，涂上玉米淀粉粘合剂，人工挂上里纸，在上胶机裱合成瓦楞纸板；上胶机的涂胶辊表面镀铬，厚度为0.5mm，并经磨削加工；(3)覆层：将裱好的单层瓦楞纸板进行叠加粘结完成覆层；(4)烘干定型：采用蒸汽干燥、电热干燥、远红外干燥、微波干燥四种干燥方式中的一种进行烘干定型；(5)冷却：采用风扇式冷却方式进行冷却；(6)压线：按照需要规格进行分纸压线；(7)纵切和横切：根据压线，采用横切机和纵切机来完成...
【技术特征摘要】
1.一种阻燃瓦楞纸板的制造工艺，其特征在于，包括如下步骤：(1)制胶：将水、淀粉、碱用、树酯胶粘剂、硼砂按比例混合充分搅拌成胶；(2)上粘胶裱纸：瓦楞原纸经过压楞后，由传递装置将其送入上胶机，涂上玉米淀粉粘合剂，人工挂上里纸，在上胶机裱合成瓦楞纸板；上胶机的涂胶辊表面镀铬，厚度为0.5mm，并经磨削加工；(3)覆层：将裱好的单层瓦楞纸板进行叠加粘结完成覆层；(4)烘干定型：采用蒸汽干燥、电热干燥、远红外干燥、微波干燥四种干燥方式中的一种进行烘干定型；(5)冷却：采用风扇式冷却方式进行冷却；(6)压线：按照...
【专利技术属性】
技术研发人员：徐俊，谢云飞，谢剑，
申请(专利权)人：芜湖市新大桥包装有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。