一种箱板纸用纸浆制造技术

本发明专利技术涉及纸板制造领域，提供一种箱板纸用纸浆，其原料组分重量配比为：硫酸盐木浆20～30份，稻麦草浆10～15份，棉杆浆10～20份，废纸浆20～30份，矿物纤维5～10份，胶原纤维5～10份。该发明专利技术具有的优点在于以废纸浆、矿物纤维和皮革固体废弃物中的胶原纤维代替部分原生木浆，减少了造纸过程中原生木浆的用量，同时为废纸浆及皮革固体废弃物的处理找到了一条新的途径，减轻了对环境的压力，此外，胶原纤维以及矿物纤维的添加能明显提高纸张的抗张指数、撕裂指数和耐折度，保证了箱板纸的质量。

Pulp paper pulp

The invention relates to the field of paperboard manufacturing, and provides a pulp for carton and paper. The weight ratio of raw material components is 20~30 parts: sulfate wood pulp, 10~15 wheat straw pulp, 10~20 cotton stalk pulp, 20~30 waste pulp, 5~10 mineral fiber and 5~10 collagen fiber. The invention has the advantages that the waste paper pulp, mineral fiber and leather solid waste in collagen fibers instead of part of original pulp, reduce the amount of original pulp in papermaking process, at the same time for the treatment of waste paper pulp and leather solid waste to find a new way to reduce the pressure on the environment, in addition, collagen fiber and the addition of mineral fiber can significantly improve the paper tensile index, tear index and folding endurance, ensure the quality of the carton.

【技术实现步骤摘要】
一种箱板纸用纸浆
本专利技术属于板纸制造领域，尤其是涉及一种箱板纸用纸浆。
技术介绍
箱板纸的制备原料一般采用原生木浆和废纸木浆两种原料，原生木浆具有更好的耐破度和性能，但成本较高，废纸木浆的强度较差，从环保的角度讲，造纸行业的趋势是尽可能减少原生木浆的使用，节约不可再生资源，尽可能地回收利用可再生资源。因此，为了兼顾箱板纸的外观质量和强度指标以及环保的要求，有必要提供一种木浆使用量少，又能保证箱板纸质量的纸浆。
技术实现思路
本专利技术的目的是提供一种箱板纸用纸浆，木浆的使用量少，制造的箱板纸强度高。为实现上述的专利技术目的，本专利技术的技术方案如下：一种箱板纸用纸浆，其原料组分重量配比为：硫酸盐木浆20～30份，稻麦草浆10～15份，棉杆浆10～20份，废纸浆20～30份，矿物纤维5～10份，胶原纤维5～10份。进一步，所述废纸浆为短纤维废纸浆。进一步，所述矿物纤维为硅灰石矿细粉。进一步，所述胶原纤维取自皮革固体废弃物。本专利技术具有的优点和积极效果是：以废纸浆、矿物纤维和皮革固体废弃物中的胶原纤维代替部分原生木浆，减少了造纸过程中原生木浆的用量，同时为废纸浆及皮革固体废弃物的处理找本文档来自技高网...

【技术保护点】
一种箱板纸用纸浆，其特征在于：其原料组分重量配比为：硫酸盐木浆10～15份，稻麦草浆10～15份，棉杆浆10～20份，废纸浆20～30份，矿物纤维5～10份，胶原纤维5～10份。

【技术特征摘要】
1.一种箱板纸用纸浆，其特征在于：其原料组分重量配比为：硫酸盐木浆10～15份，稻麦草浆10～15份，棉杆浆10～20份，废纸浆20～30份，矿物纤维5～10份，胶原纤维5～10份。2.根据权利要求1所述的箱...

【专利技术属性】