The invention discloses an automobile glass antifogging agent and a preparation method. The following components of the antifogging agent are sodium silicate, twelve alkyl benzene sulfonate, polyethylene glycol, inorganic nanoparticles, polyvinylpyrrolidone, isopropanol, ethanol, water and defoamer. The preparation method of sodium silicate, sodium twelve and polyethylene glycol is added to water, mixing, mixed liquid; adding ethanol and isopropyl alcohol in the mixture, heating after adding inorganic nanoparticles and defoaming agent, stirring 20 30 minutes to obtain a mixed solution of two; finally in the mixed liquid 2 adding polyethylene pyrrolidone, at room temperature for 3 5 hours to get the car glass antifogging agent. The automobile glass antifogging agent provided by the invention has good antifogging performance at high temperature and low temperature, and has long duration of anti fogging.
【技术实现步骤摘要】
一种汽车玻璃防雾剂及其制备方法
本专利技术属于玻璃防雾领域吗，具体涉及一种汽车玻璃防雾剂及其制备方法。
技术介绍
在冬季或夏季阴雨天，汽车内外环境存在较大的温度差异，当玻璃内表面温度达到露点温度时，水汽便在玻璃表面结露，形成密密麻麻的小水滴层而阻挡视野，汽车玻璃起雾给驾驶人员安全行驶带来极大困扰，尤其是汽车前窗、挡风玻璃和内后视镜起雾时，会严重影响驾驶员的视线，为安全行车带来隐患。玻璃防雾剂的研究目前处在积极开发的阶段，各国都展开了对防雾剂的研究，特别是随着在汽车行业的发展，玻璃方面的应用日益明显。当前市场上普遍采用的防雾剂是基于表面活性剂的防雾产品，表面活性剂易随水蒸汽凝结形成的水膜流动而流失，且不耐擦拭，使用寿命短。
技术实现思路
本专利技术的目的在于为了克服以上现有技术的不足而提供一种汽车玻璃防雾剂及其制备方法，提高汽车玻璃在高温与低温环境下的防雾效果。本专利技术的技术方案如下：一种汽车玻璃防雾剂，以重量份计包括以下组分：硅酸钠2-4份，十二烷基苯磺酸钠1-2份，聚乙二醇3-7份，无机纳米颗粒3-6份，聚乙烯吡咯烷酮1-3份，异丙醇5-10份，乙醇20-30份，...
【技术保护点】
一种汽车玻璃防雾剂，其特征在于，以重量份计包括以下组分：硅酸钠2‑4份，十二烷基苯磺酸钠1‑2份，聚乙二醇3‑7份，无机纳米颗粒3‑6份，聚乙烯吡咯烷酮1‑3份，异丙醇5‑10份，乙醇20‑30份，水5‑10份，消泡剂0.5‑1份。
【技术特征摘要】
1.一种汽车玻璃防雾剂，其特征在于，以重量份计包括以下组分：硅酸钠2-4份，十二烷基苯磺酸钠1-2份，聚乙二醇3-7份，无机纳米颗粒3-6份，聚乙烯吡咯烷酮1-3份，异丙醇5-10份，乙醇20-30份，水5-10份，消泡剂0.5-1份。2.根据权利要求1所述的汽车玻璃防雾剂，其特征在于，所述聚乙二醇为聚乙二醇800。3.根据权利要求1所述的汽车玻璃防雾剂，其特征在于，所述无机纳米颗粒为纳米二氧化硅。4.根据权利要求1所述的汽车玻璃防雾剂，其特征在于，所述消泡剂为乳化硅油。5.权利要求1所述的汽车玻璃防雾剂的制备方法，其特征在于，包括以下步骤：步骤一，将硅酸钠，十二烷基苯...
【专利技术属性】
技术研发人员：冉宏敏，
申请(专利权)人：苏州纽东精密制造科技有限公司，
类型：发明
国别省市：江苏,32