The invention relates to the field of waterproof materials, in particular, provides an asphalt waterproof material and a preparation method thereof, and a waterproof coil material comprising the asphalt waterproof material and a preparation method thereof. The asphalt waterproof material mainly consists of the following raw materials prepared by 90# 30, 10# 20 asphalt asphalt 10 15 copies, 10 copies, 6 softening oil rubber 12 18 copies, 1 copies and 0.5 SBS talc 30 40. The waterproof roll is mainly made from the tire base cloth and the asphalt waterproof material. The waterproofing membrane has the advantages of high and low temperature performance, good waterproof performance and low cost.
【技术实现步骤摘要】
沥青防水材料及其制备方法、包含该沥青防水材料的防水卷材及其制备方法
本专利技术涉及防水材料领域，具体而言，涉及一种沥青防水材料及其制备方法、包含该沥青防水材料的防水卷材及其制备方法。
技术介绍
将沥青类或高分子类防水材料浸渍在胎基布上制成的防水材料产品，以卷材的形式提供，称为防水卷材。防水卷材是主要用于建筑墙体、屋面、以及隧道、公路、垃圾填埋场等处，起到抵御外界雨水、地下水渗漏的柔性建材产品，作为工程基础与建筑物之间无渗漏连接，是整个工程防水的第一道屏障，对整个工程起着至关重要的作用。现有的应用于防水卷材中的沥青防水材料多为SBS(StyreneicBlockCopolymers，苯乙烯系嵌段共聚物)改性沥青防水材料或APP(AtacticPolypropylene，无规聚丙烯)改性沥青防水材料。其中，SBS改性沥青防水卷材的低温性能较好，Ⅰ类的SBS改性沥青防水卷材在-20℃不流淌，然而其高温性能较差，最高仅能承受90℃的高温；APP改性沥青防水卷材的高温性能较好，Ⅰ类的APP改性沥青防水卷材在105℃不流淌，然而其低温性能较差，最低仅能承受-7℃的低温。因此，...
【技术保护点】
一种沥青防水材料，其特征在于，主要由以下重量份的原料制备而成：90#沥青20‑30份、10#沥青10‑15份、软化油6‑10份、橡胶12‑18份、SBS 0.5‑1份和滑石30‑40份。
【技术特征摘要】
1.一种沥青防水材料，其特征在于，主要由以下重量份的原料制备而成：90#沥青20-30份、10#沥青10-15份、软化油6-10份、橡胶12-18份、SBS0.5-1份和滑石30-40份。2.根据权利要求1所述的沥青防水材料，其特征在于，主要由以下重量份的原料制备而成：90#沥青22-29份、10#沥青11-14份、软化油7-9份、橡胶12-17份、SBS0.5-0.9份和滑石32-39份。3.根据权利要求1所述的沥青防水材料，其特征在于，主要由以下重量份的原料制备而成：90#沥青24-28份、10#沥青12-13份、软化油7-8份、橡胶13-16份、SBS0.6-0.8份和滑石35-38份。4.权利要求1-3任一项所述的沥青防水材料的制备方法，其特征在于，包括以下步骤：首先将配方量的90#沥青、10#沥青和软化油混合均匀得到预混料，然后将预混料和粉碎后的配方量的橡胶混合均匀得到第一改性预混料，再将第一改性预混料和配方量的SBS混合均匀得到第二改性预混料，最后将第二改性预混料和粉碎后的配方量的滑石混合均匀即可。5.根据权利要求4所述的沥青防水材料的制备方法，其特征在于，包括以下步骤：首先将配方量的9...
【专利技术属性】
技术研发人员：吕航杰，
申请(专利权)人：天津市鹏腾新型建筑材料有限公司，
类型：发明
国别省市：天津,12