The invention provides a modified carbon fiber / benzoxazine composite material and a preparation method thereof. The method comprises: adding carbon fiber into nitrate, after stirring reflux in the oil bath, the supernatant was removed after filtration, washed to neutral, drying to obtain the modified carbon fiber; benzoxazine and the resulting modified carbon fiber in a solvent at room temperature, ultrasonic, and evaporating the solvent, the first heating by melt mixing system; the molten mixture is poured into a mold, second heating, vacuum pumping air bubbles, after third heating, and then solidified to obtain the modified carbon fibers / benzoxazine composites. The modified carbon fiber / benzoxazine composite material provided by the invention improves the thermal and mechanical properties of the composites.
【技术实现步骤摘要】
一种改性碳纤维/苯并噁嗪复合材料及其制备方法
本专利技术涉及复合材料，更具体地，涉及一种改性碳纤维/苯并噁嗪复合材料及其制备方法。
技术介绍
苯并噁嗪是一类新型的酚醛树脂，它与普通酚醛树脂的区别在于成型固化过程中没有小分子放出，体积变化率接近为0，并具有良好的分子设计性。苯并噁嗪的制备以酚类、醛类和伯胺类化合物为原料反应制得。苯并噁嗪固化物具有良好的耐热性、耐湿性、机械性能和电气性能，其缺点为固化温度高。由于体积收缩率低、吸湿率低，耐热性能好等优异性能，苯并噁嗪树脂被广泛应用于复合材料基体树脂、电子封装材料和电绝缘材料等领域。但传统的苯并噁嗪树脂也存在脆性较大、加工性能差、交联得到的聚合物分子量较小等，限制了其在工业中的应用。碳纤维因比表面积小，表面化学惰性和憎液性等缺点，使其与苯并噁嗪树脂的结合力不够，降低了复合材料的性能。
技术实现思路
本专利技术提供了一种碳纤维表面改性苯并噁嗪树脂的方法，改善了苯并噁嗪的热性能和力学性能。本专利技术提供了一种制备改性碳纤维/苯并噁嗪复合材料的方法，包括：将碳纤维加入到硝酸中，搅拌后置于油浴中回流，除去上清液后抽滤，水洗至中性，干...
【技术保护点】
一种制备改性碳纤维/苯并噁嗪复合材料的方法，其特征在于，包括：将碳纤维加入到硝酸中，搅拌后置于油浴中回流，除去上清液后抽滤，水洗至中性，干燥得到改性碳纤维；将苯并噁嗪和得到的所述改性碳纤维溶于溶剂中，室温超声，蒸掉所述溶剂，进行第一加热，得到熔融混合体系；将所述熔融混合体系倒入模具中，进行第二加热，真空抽气泡，抽完后进行第三加热，然后固化，得到改性碳纤维/苯并噁嗪复合材料。
【技术特征摘要】
1.一种制备改性碳纤维/苯并噁嗪复合材料的方法，其特征在于，包括：将碳纤维加入到硝酸中，搅拌后置于油浴中回流，除去上清液后抽滤，水洗至中性，干燥得到改性碳纤维；将苯并噁嗪和得到的所述改性碳纤维溶于溶剂中，室温超声，蒸掉所述溶剂，进行第一加热，得到熔融混合体系；将所述熔融混合体系倒入模具中，进行第二加热，真空抽气泡，抽完后进行第三加热，然后固化，得到改性碳纤维/苯并噁嗪复合材料。2.根据权利要求1所述的方法，其特征在于，将碳纤维加入到硝酸中包括将0.5-2g碳纤维加入到300ml70％浓硝酸中。3.根据权利要求1所述的方法，其特征在于，将碳纤维加入到硝酸后搅拌的时间为20-40min。4.根据权利要求1所述的方法，其特征在于，回流的温度为...
【专利技术属性】
技术研发人员：不公告发明人，
申请(专利权)人：洛阳尖端技术研究院，洛阳尖端装备技术有限公司，
类型：发明
国别省市：河南,41
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。