The invention provides a three yuan nano rare earth complex composite heat stabilizer, which comprises the following components: the quality of a rare earth stearic acid two benzoyl methane three yuan nano complex 1 ~ 3, 10 ~ 50 calcium stearate, zinc stearate is 10 ~ 40, 25 ~ 50 auxiliary heat stabilizer. The rare earth stearic acid two benzoyl methane complex is three yuan three yuan nano nano rare earth complexes formed by the rare earth salt, stearic acid and two benzoyl methane as raw materials for the preparation of the. The thermal stabilizer of the invention improves the thermal stability of the compound heat stabilizer by adding nano rare earth complex in the zinc calcium heat stabilizer.
【技术实现步骤摘要】
一种三元纳米稀土络合物复合热稳定剂
本专利技术属于PVC热稳定剂领域，涉及一种三元纳米稀土络合物复合热稳定剂。
技术介绍
聚氯乙烯(PVC)是五大通用塑料之一，但其热稳定性差，易分解，在加工过程中必须加入热稳定剂。PVC用热稳定剂的品种多样，目前常用的品种包括铅盐类、钙锌皂类、有机锡类、稀土类、复合稳定剂等，各种稳定剂各具特色。钙锌热稳定剂由钙盐、锌盐、润滑剂、抗氧剂等为主要组分采用特殊复合工艺而合成，是一种良好的无毒稳定剂，它又可分为粉体钙锌稳定剂与液体钙锌稳定剂，粉体钙锌稳定剂制备简单，包装和运输方便，应用广泛。为了提高粉体钙锌热稳定剂的性能，通常在单一热稳定剂的基础上，进行科学复合，制成复合型热稳定剂，可以充分利用各种热稳定剂的优势，提高综合热稳定剂性能。中国专利《一种钙锌复合阻燃热稳定剂》(申请号：201310303263.5)公布了一种用于PVC的兼具阻燃性能的无毒钙锌复合热稳定剂，该复合材料主要由钙锌热稳定剂、微米或纳米级活化沸石、润滑剂、辅助热稳定剂和抗氧剂组成；中国专利《一种硬质PVC用稀土复合热稳定剂》(申请号：201310040221.7)公布...
【技术保护点】
一种三元纳米稀土络合物复合热稳定剂，其特征在于，包括如下质量份的组份：稀土‑硬脂酸‑二苯甲酰甲烷三元纳米络合物1～3份，硬脂酸钙10～50份，硬脂酸锌10～40份，辅助热稳定剂25～50份，所述稀土‑硬脂酸‑二苯甲酰甲烷三元纳米络合物是由稀土盐、硬脂酸和二苯甲酰甲烷为原料制备而成的纳米级的三元稀土络合物。
【技术特征摘要】
1.一种三元纳米稀土络合物复合热稳定剂，其特征在于，包括如下质量份的组份：稀土-硬脂酸-二苯甲酰甲烷三元纳米络合物1～3份，硬脂酸钙10～50份，硬脂酸锌10～40份，辅助热稳定剂25～50份，所述稀土-硬脂酸-二苯甲酰甲烷三元纳米络合物是由稀土盐、硬脂酸和二苯甲酰甲烷为原料制备而成的纳米级的三元稀土络合物。2.根据权利要求1所述的三元纳米稀土络合物复合热稳定剂，其特征在于，所述辅助热稳定剂为环氧大豆油、季戊四醇、亚磷酸酯的一种或几种的混合物。3.一种权利要求1所述的稀土-硬脂酸-二苯甲酰甲烷三元纳米络合物的制备方法，其特征在于，包括如下步骤：(1)准确称取稀土盐、硬...
【专利技术属性】
技术研发人员：李军伟，张宝行，王佳欣，李哲辉，
申请(专利权)人：天津城建大学，
类型：发明
国别省市：天津,12
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。