The invention discloses a cracking resistance of concrete expansive agent is composed of the following components: the weight of a fat lime 5 15 copies, 20 copies, 15 alumina Magnesium Oxide 6 10 copies, 45 copies, 25 gypsum and 10 calcium chloride 15, defoaming agent 5, 3 cryolite powder 3 5 copies, 4 copies of 2 stabilizer. The invention has the advantages of high expansion energy, stable performance, low alkali content, low volume, low production cost, excellent product performance, and technical indicators meeting the requirements of the national standard. Cracking resistance of concrete expansive cement hydration rate and reaction rate are basically the same, in each period of concrete curing reaction expansion rate is moderate, stable long-term performance of concrete, can effectively prevent the crack of concrete, is formulated and the impermeability of concrete admixtures to crack.
【技术实现步骤摘要】
一种混凝土抗裂膨胀剂
本专利技术涉及建筑用混凝土外加剂领域，具体是一种混凝土抗裂膨胀剂。
技术介绍
混凝土外加剂，简称外加剂，是指在拌制混凝土拌合前或拌合过程中掺入用以改善混凝土性能的物质。由于外加剂能有效地改善混凝土的性能，而且具有良好的经济效益，在许多国家都得到广泛的应用，在工程中的应用越来越受到重视，成为混凝土中不可或缺的材料。其中膨胀剂是混凝土外加剂中的一种，它加在混凝土中，当混凝土凝结硬化时，随之体积膨胀，起补偿收缩和张拉钢筋产生预应力以及充分填充混凝土间隙的作用。目前膨胀剂市场比较混乱，膨胀性能不稳定，无法满足高性能混凝土的要求。
技术实现思路
本专利技术提供了一种混凝土抗裂膨胀剂，以解决上述技术问题。一种混凝土抗裂膨胀剂，由以下重量份的成分组成：脂化生石灰5-15份、氧化铝15-20份、氧化镁6-10份、石膏25-45份、氯化钙10-15份、消泡剂3-5份、冰晶石粉3-5份、稳定剂2-4份。优选的，所述的混凝土抗裂膨胀剂，由以下重量份的成分组成：脂化生石灰10份、氧化铝18份、氧化镁8份、石膏35份、氯化钙13份、消泡剂4份、冰晶石粉4份、稳定剂3份。本专利技术的有益效果：本专利技术具有膨胀能高、性能稳定、碱含量低、掺量低、生产成本低廉、产品性能优良且技术指标符合国家标准规定等优点。混凝土抗裂膨胀剂的膨胀速率与水泥水化反应速率基本一致，在混凝土固化反应的各个时期膨胀速率适中，混凝土长期性能稳定，能有效的防止混凝土裂纹的出现，是配制抗裂和抗渗混凝土的理想外加剂。具体实施方式以下对本专利技术的实施例进行详细说明，但是本专利技术可以由权利要求限定和覆盖...
【技术保护点】
一种混凝土抗裂膨胀剂，其特征在于，由以下重量份的成分组成：脂化生石灰5‑15份、氧化铝15‑20份、氧化镁6‑10份、石膏25‑45份、氯化钙10‑15份、消泡剂3‑5份、冰晶石粉3‑5份、稳定剂2‑4份。
【技术特征摘要】
1.一种混凝土抗裂膨胀剂，其特征在于，由以下重量份的成分组成：脂化生石灰5-15份、氧化铝15-20份、氧化镁6-10份、石膏25-45份、氯化钙10-15份、消泡剂3-5份、冰晶石粉3-5份、稳定...
【专利技术属性】
技术研发人员：殷永生，
申请(专利权)人：桐城市永锦建筑工程有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。