一种高硬度的钧瓷宝石蓝釉及其制备方法技术
A high hardness sapphire blue porcelain glaze and preparation method thereof
The invention discloses a high hardness sapphire blue glaze porcelain, which is characterized by comprising the following raw materials prepared by the 30 36 yellow feldspar and quartz, calcite 20 28 12 18 copies, 18 copies, 12 wollastonite burn talc 4 6, Zinc Oxide 3 5 copies, 1.5 copies of 0.5 tin oxide and copper oxide 0.5 1.5 copies, 0.7 copies, 0.3 cobalt oxide kaolin 3 5. The preparation method of high hardness sapphire blue glaze porcelain, which comprises the following steps: (1) the raw materials are crushed together in a ball mill, add water to the concentration of glaze reached 53 54%, 7 wet milling 8 hours after slurry wet grinding 250 320 mesh sieve to get glaze body; (2) dipping 1 2 times; (3) burning, burning temperature of 1200 DEG C 1240.
【技术实现步骤摘要】
一种高硬度的钧瓷宝石蓝釉及其制备方法
本专利技术涉及钧瓷制造
，具体涉及一种高硬度的钧瓷宝石蓝釉及其制备方法。
技术介绍
钧瓷发端于东汉，是宋代五大名窑瓷器之一，中国传统制瓷工艺中的珍品，被称为国宝、瑰宝。以独特的窑变艺术而著称于世，素有“黄金有价钧无价”和“家有万贯，不如钧瓷一件”的美誉。钧瓷是河南省许昌市禹州市神垕镇独有的国宝瓷器，凭借其古朴的造型、精湛的工艺、复杂的配釉、“入窑一色出窑万彩”的神奇窑变，湖光山色、云霞雾霭、人兽花鸟虫鱼等变化无穷的图形色彩和奇妙韵味，被誉为中国“五大名瓷”之首。现有技术中，宝石蓝釉的配方及其制备方法还很少，且机械强度低，烧制不易。在烧制的过程中有50％左右的产品会报废掉，成品率低，因此对原料的浪费巨大，制作成本太高。
技术实现思路
本专利技术提供了一种原料及配比新颖的高硬度的钧瓷宝石蓝釉及其制备方法以解决现有钧瓷宝石蓝釉的配方及制备方法少，机械强度低，成品率低，制作成本和制作难度高的问题。本专利技术的目的是以下述技术方案实现的：一种高硬度的钧瓷宝石蓝釉，它是由以下重量份的原料制备而成：黄长石30-36份、石英20-28份、方...
【技术保护点】
一种高硬度的钧瓷宝石蓝釉，其特征在于：它是由以下重量份的原料制备而成：黄长石30‑36份、石英20‑28份、方解石12‑18份、硅灰石12‑18份、烧滑石4‑6份、氧化锌3‑5份、氧化锡0.5‑1.5份、氧化铜0.5‑1.5份、氧化钴0.3‑0.7份、高岭土3‑5份。
【技术特征摘要】
1.一种高硬度的钧瓷宝石蓝釉，其特征在于：它是由以下重量份的原料制备而成：黄长石30-36份、石英20-28份、方解石12-18份、硅灰石12-18份、烧滑石4-6份、氧化锌3-5份、氧化锡0.5-1.5份、氧化铜0.5-1.5份、氧化钴0.3-0.7份、高岭土3-5份。2.根据权利要求1所述的高硬度的钧瓷宝石蓝釉，其特征在于：它是由以下重量份的原料制备而成：黄长石33份、石英24份、方解石15份、硅灰石15份、烧滑石5份、氧化锌4份、氧化锡1份、氧化铜1份、氧化钴0.5份、高岭土4份。3.一种如权利要求1或2所述的高硬度的钧瓷...
【专利技术属性】
技术研发人员：崔松伟，温红超，崔世豪，崔鹏豪，
申请(专利权)人：禹州市锦丰源瓷业有限公司，
类型：发明
国别省市：河南,41