The invention relates to the field of composite paper, which is a preparation process of a composite paper. The purpose of the invention is to prepare high-strength waterproof and printable special paper, so as to meet the special requirements for marking materials in nuclear power plants and related industries. The composite paper preparation steps: 1, to a certain thickness of PET high temperature resistant polyester film as substrate, the hot melt glue on the substrate side; 2, on the substrate glue placed in a drying box for drying treatment; 3, the quality grade is A writing paper covered on the rubber surface on the base plate. Press under pressure; 4, hot melt adhesive on the substrate on the other side of a rubber; 5, again will be placed in the substrate drying box for drying treatment; 6, the quality level of A writing paper covered on second times on the rubber surface substrate, were pressed under certain pressure 7, in the composite paper; both sides after the synthesis of waterproof paint spraying, baking special paper synthesis, can get the finished product.
【技术实现步骤摘要】
一种高强度防水打印纸的制备方法
本专利技术涉及复合纸领域，具体是复合纸的制备工艺。
技术介绍
目前国内核电厂由于设备隔离工作的需要，需要打印并悬挂设备标识牌。由于悬挂环境比较好复杂，故要求标识牌具备以下三个特种性能：具有一定的强度，耐撕性能；防水性能；可在激光打印机打印。现在国内核电站的设备标识牌通用处理方法如下：选用厚度高一点且可打印的纸，通过激光打印机将设备信息打印到纸上，然后在纸上钻孔后，悬挂于设备上。一方面这样的设备标识牌强度不够，经常损坏，设备标识遗失；另一方面当标识牌遇到水时，字迹变得不清晰。这样的情况给核电厂带来了极大的安全隐患。本专利技术申请是通过一种合成的方法制备出高强度防水可打印的特种纸，以满足核电站及有关工业领域对标识牌的特殊要求。
技术实现思路
本专利技术通过以下复合工艺，制备了一种高强度防水可打印特种纸。该特种纸复合工艺，依次包括以下步骤：(一)将一定厚度的PET耐高温聚酯薄膜作为基板（1），将热熔胶在基板一面进行上胶（2）；(二)将上胶的基板放置在烘干箱中进行烘干处理（3）；(三)将质量等级为A的书写纸覆盖于上胶面的基板（4），在一定的压力...
【技术保护点】
如权利要求（1）所述的基板，期特征在于：所述PET耐高温聚酯薄膜厚度0.20‑0.50mm。
【技术特征摘要】
1.如权利要求（1）所述的基板，期特征在于：所述PET耐高温聚酯薄膜厚度0.20-0.50mm。2.如权利要求（2）所述的上胶，其特征在于：采用喷胶的方式进行上胶，所述喷胶速率为0.5ml/s，热熔胶的熔胶温度为135℃。3.如权利要求（3）所述的复合工艺，其特征在于：烘干...