The invention discloses a kind of silicon rubber material, in particular a kind of flame retardant and heat-resistant silicone rubber and a preparation method. The weight of the raw materials for the vinyl content of 0.12% were 100, 30 fumed silica 50, two methyl two methoxy silane 3 6 copies, 6 copies, 3 hydroxy silicone oil vinyltrimethoxysilane 0.2 0.6, stearic acid 18010.2 0.4, Zinc Oxide 1 10 copies, ten bromo two benzene ethane 20 30 copies, 2 copies of 1 cerium oxide. The formula and method mentioned above, the reasonable selection of various raw materials and reasonable matching of various raw materials, plus special preparation methods and preparation process of various parameters were strictly controlled, products made through the actual test has good flame retardant properties, and has characteristic of high temperature resistance, hardness, good strength and processing performance, fully meet the requirements to use high temperature flame retardant cable.
【技术实现步骤摘要】
一种阻燃耐热硅橡胶及其制备方法
本专利技术涉及一种硅橡胶材料的制造，具体地说是一种阻燃耐热硅橡胶及其制备方法。
技术介绍
硅橡胶具备良好的耐高低温、耐臭氧、耐候性、绝缘性及生产惰性等很多优异的性能，在国民经济的各个领域有着广泛的应用。气相法白炭黑填充的硅橡胶具有较好的电绝缘特性以及其优异的加工成型性能决定了它可以作为电缆使用。但是要应用在特殊的环境下，如高温环境，硅橡胶的耐高温性能和阻燃性能就达不到要求，因此，研究耐高温阻燃硅橡胶具有十分积极的意义。
技术实现思路
本专利技术所要解决的技术问题是提供一种阻燃等级高，同时具有较好的耐高温特性、硬度、强度和加工性能的阻燃耐热硅橡胶及其制造方法。为了解决上述技术问题，本专利技术的阻燃耐热硅橡胶，其原料组成的重量份为：乙烯基摩尔含量0.12%的生胶100份气相白炭黑30-50份二甲基二甲氧基硅烷3-6份羟基硅油3-6份乙烯基三甲氧基硅烷0.2-0.6份硬脂酸18010.2-0.4份氧化锌1-10份十溴二苯乙烷20-30份氧化铈1-2份。一种上述阻燃耐热硅橡胶的制备方法，包括以下步骤：a、将乙烯基摩尔含量0.12%的甲基乙烯基生...
【技术保护点】
一种阻燃耐热硅橡胶，其特征在于，其原料组成的重量份为：乙烯基摩尔含量0.12%的生胶 100份气相白炭黑 30‑50份二甲基二甲氧基硅烷 3‑6份羟基硅油 3‑6份乙烯基三甲氧基硅烷 0.2‑0.6份硬脂酸1801 0.2‑0.4份氧化锌 1‑10份十溴二苯乙烷 20‑30份氧化铈...
【技术特征摘要】
1.一种阻燃耐热硅橡胶，其特征在于，其原料组成的重量份为：乙烯基摩尔含量0.12%的生胶100份气相白炭黑30-50份二甲基二甲氧基硅烷3-6份羟基硅油3-6份乙烯基三甲氧基硅烷0.2-0.6份硬脂酸18010.2-0.4份氧化锌1-10份十溴二苯乙烷20-30份氧化铈1-2份。2.一种如权利要求1所述阻燃耐热硅橡胶的制备方法，其特征在于，包括以下步骤：a、将乙烯基摩尔含量0.12%的甲基乙烯基生胶加入到捏合机中搅拌2-4分钟；b、将白炭黑、硬脂酸1801、二甲基二甲氧基硅...
【专利技术属性】
技术研发人员：施贤斌，徐文俊，宋顺刚，
申请(专利权)人：江苏天辰新材料股份有限公司，
类型：发明
国别省市：江苏,32