The invention discloses a preparation method of a polyester composition, a polyester composition prepared by the method and the use of a polyester composition. The method is mainly by two yuan, aromatic carboxylic acid and aliphatic diols by esterification, then further polymerization; adding antimony compounds, manganese compounds and phosphorus compounds at the beginning of the esterification reaction after polymerization or before, in the polymerization reactor inherent viscosity up to 0.5dl/g to the end of the reaction in the polymerization time, adding copper in the reactant in polyester compounds. The polyester composition produced by this method is less than 5wt% at 300 C. 6hr after heat treatment at the oxygen gas mixture of oxygen concentration of 1vol%. The hue value of L is above 50, and the a value is below 4. The polyester composition can be used in the fields of thin film and the like.
【技术实现步骤摘要】
一种聚酯组合物的制备方法、聚酯组合物及其用途
本专利技术涉及一种凝胶率低、色调优异的聚酯组合物的制备方法，由该方法制备得到的聚酯组合物，以及该聚酯组合物的用途。
技术介绍
聚酯，特别是聚对苯二甲酸乙二醇酯、聚对苯二甲酸丙二醇酯、聚对苯二甲酸丁二醇酯等，由于具有优异的机械、物理、化学性能而被广泛地用于纤维、薄膜以及其他模塑产品的生产。然而，大部分的聚酯在高温条件下都会发生热氧降解和热分解，在热氧降解反应中，氧自由基攻击聚酯苯环上的氢，生成过氧化官能团，该过氧化官能团不稳定又会分解生成自由基，所生成的自由基作为架桥点和聚酯热分解后的产物生成架桥结构，即发生交联反应，形成不熔性胶状物，一般也称之为凝胶。在制膜工程中，凝胶的产生可能导致熔体过滤网频繁更换，造成原料浪费和成本的上升。另外，薄膜上出现凝胶的疵点导致薄膜品质下降，用途受限。为了使聚酯能够更好的应用于制膜领域并提高薄膜品质，人们进行了许多研究来解决聚酯凝胶化的缺点。目前研究的方法主要有在聚酯的聚合阶段添加一些具有还原效果的金属助催化剂，以期获得较低的聚酯凝胶率。例如，日本专利特开2005-314643以及特开20...
【技术保护点】
一种聚酯组合物的制备方法，先由芳香族二元羧酸与脂肪族二元醇进行酯化反应，然后进一步进行聚合反应，其特征在于：在酯化反应结束后或聚合反应开始前添加锑化合物、锰化合物和磷化合物，在聚合反应物固有粘度达到0.5dl/g到聚合反应终了的时间内，在聚酯反应物里添加铜化合物。
【技术特征摘要】
1.一种聚酯组合物的制备方法，先由芳香族二元羧酸与脂肪族二元醇进行酯化反应，然后进一步进行聚合反应，其特征在于：在酯化反应结束后或聚合反应开始前添加锑化合物、锰化合物和磷化合物，在聚合反应物固有粘度达到0.5dl/g到聚合反应终了的时间内，在聚酯反应物里添加铜化合物。2.根据权利要求1所述聚酯组合物的制备方法，其特征在于：所述铜化合物为醋酸铜、硬脂酸铜、苯二甲酸铜、硫酸铜、柠檬酸铜、醋酸亚铜、氧化铜、氢氧化铜中的一种或几种。3.根据权利要求1或2所述聚酯组合物的制备方法，其特征在于：所述铜化合物的添加量以铜元素计相当于聚酯组合物的5～200ppm。4.根据权利要求1所述聚酯组合物...
【专利技术属性】
技术研发人员：祁华，梅涛锋，旦浩一，
申请(专利权)人：东丽纤维研究所中国有限公司，
类型：发明
国别省市：江苏,32