一种PI基板及其制备方法、显示装置制造方法及图纸
A PI substrate and its preparation method and display device
The invention provides a PI substrate and a preparation method thereof, display device, including: in the edge area of the substrate to form a first release film; forming a first layer of polyamic acid PAA film in the first film and the substrate; the edge region of the first stripping mold release film and covered on the the first film on the first layer of PAA film, the edge region of the substrate is exposed; the first layer of PAA film exposed to the edge region of the substrate and the substrate of the imidization process, the formation of the PI substrate, so as to solve the existing PI coating PI film thickness uneven edge problem when there are.
【技术实现步骤摘要】
一种PI基板及其制备方法、显示装置
本专利技术涉及显示器
，特别是涉及一种PI基板及其制备方法、显示装置。
技术介绍
近年来随着柔性显示技术迅猛发展，各显示面板厂商纷纷展出自己的样机，同时也积极的布局自己的柔性显示生产线和量产线，柔性显示技术逐渐从研发走向量产，使柔性显示技术得到了快速发展。目前柔性基板分为两种，一种是三明治结构聚酰亚胺(Polyimide，PI)基板，另一种是单层PI基板，上述两种PI基板均存在涂覆聚酰亚胺PI时，由于PI扩散不均匀，从而在PI基板边缘会产生膜厚度不均匀区域。由于PI边缘的厚度不均，干燥固化时会产生残留溶剂、固化不完全和产生孔洞等肉眼不可见的缺陷，从而影响了PI基板的良率。
技术实现思路
本专利技术提供了一种PI基板及其制备方法、显示装置，以解决现有涂布PI时存在PI膜边缘厚度不均匀的问题。为了解决上述问题，本专利技术公开了一种PI基板的制备方法，包括：在基板的边缘区域形成第一离型膜；在所述第一离型膜以及所述基板上形成第一层聚酰胺酸PAA膜；剥离所述边缘区域的第一离型膜以及覆盖在所述第一离型膜上的所述第一层PAA膜，暴露所述边缘...
【技术保护点】
一种PI基板的制备方法，其特征在于，包括：在基板的边缘区域形成第一离型膜；在所述第一离型膜以及所述基板上形成第一层聚酰胺酸PAA膜；剥离所述边缘区域的第一离型膜以及覆盖在所述第一离型膜上的所述第一层PAA膜，暴露所述边缘区域的基板；对所述暴露所述边缘区域的基板及所述基板上的第一层PAA膜进行亚胺化处理，形成PI基板。
【技术特征摘要】
1.一种PI基板的制备方法，其特征在于，包括：在基板的边缘区域形成第一离型膜；在所述第一离型膜以及所述基板上形成第一层聚酰胺酸PAA膜；剥离所述边缘区域的第一离型膜以及覆盖在所述第一离型膜上的所述第一层PAA膜，暴露所述边缘区域的基板；对所述暴露所述边缘区域的基板及所述基板上的第一层PAA膜进行亚胺化处理，形成PI基板。2.根据权利要求1所述的方法，其特征在于，对所述暴露所述边缘区域的基板及所述基板上的第一层PAA膜进行亚胺化处理之后，还包括：在所述基板的边缘区域及所述基板的第一层PAA膜上形成无机层；在所述边缘区域形成第二离型膜；在所述第二离型膜以及所述无机层上形成第二层PAA膜；剥离所述边缘区域的第二离型膜以及覆盖在所述第二离型膜上的所述第二层PAA膜，暴露所述边缘区域的基板；对所述暴露所述边缘区域的基板及所述基板上的第二层PAA膜进行亚胺化处理，形成所述PI基板。3.根据权利要求2所述的方法，其特征在于，所述第二离型膜的厚度以及所述无机层的厚度均为所述第一层PAA膜厚度的一半。4.根据权利要...
【专利技术属性】
技术研发人员：郭远征，谢明哲，宋平，王有为，代伟男，汪明文，
申请(专利权)人：京东方科技集团股份有限公司，
类型：发明
国别省市：北京,11