The present invention relates to the field of marble, concrete is the use of technology with waterproof adhesive and its manufacturing method, a kind of marble, the quality includes the following components: organic fluorine silicone resin 13 15 copies, 12 copies, three paraffin 10 four ethylene amine 7 9 copies, 8 copies of 5 mixed crosslinking agent and polyvinyl alcohol from 5 7 copies, 5 copies, 3 solvent defoaming agent 1 3 copies, its manufacturing method includes the following steps: (1) melting; (2) mixing; (3) the use of defoaming, process specific steps are as follows: (1) clean; hardening; (2) (3) glue, mixed crosslinking agent can make polymer chemical bonds formed in the molecular backbone, which can be closely bonded between the various substances in the waterproof glue before use; repeated cleaning, protection of the marble surface without other foreign influence effect of waterproof glue.
【技术实现步骤摘要】
一种大理石用防水胶及其制造方法、使用工艺
本专利技术涉及大理石领域，具体是一种大理石用防水胶及其制造方法、使用工艺。
技术介绍
由于大理石是大型石材拼接使用的，在作为房间地板铺设时，遇上积水时，避免不了水下渗的问题，现有技术中多数使用胶水涂层将缝隙堵上减少下渗的情况，但是胶水失效很快，后期还是会有这种问题，因此，设计一种大理专用的防水胶很有必要。
技术实现思路
为了解决上述问题，本专利技术提出一种大理石用防水胶及其制造方法、使用工艺。一种大理石用防水胶，包括以下质量份数的组分：有机氟硅树脂13-15份、石蜡10-12份、三乙烯四胺7-9份、混合交联剂5-8份、聚乙烯醇缩丁醛5-7份、助溶剂3-5份、消泡剂1-3份。所述的混合交联剂为过氧化二异丙苯、氧化锌的混合物。所述的助溶剂为纯碱。所述的消泡剂为乳化硅油。一种大理石用防水胶的制造方法，其具体步骤如下：(1)融化：将石蜡融化，保温，然后加入有机氟硅树脂，得到混合物；(2)混合：将步骤(1)中的混合物加入三乙烯四胺、聚乙烯醇缩丁醛、助溶剂，搅拌的同时加入混合交联剂；(3)消泡：最后加入消泡剂即可。一种大理石用防水胶的使用...
【技术保护点】
一种大理石用防水胶，其特征在于：包括以下质量份数的组分：有机氟硅树脂13‑15份、石蜡10‑12份、三乙烯四胺7‑9份、混合交联剂5‑8份、聚乙烯醇缩丁醛5‑7份、助溶剂3‑5份、消泡剂1‑3份。
【技术特征摘要】
1.一种大理石用防水胶，其特征在于：包括以下质量份数的组分：有机氟硅树脂13-15份、石蜡10-12份、三乙烯四胺7-9份、混合交联剂5-8份、聚乙烯醇缩丁醛5-7份、助溶剂3-5份、消泡剂1-3份。2.根据权利要求1所述的一种大理石用防水胶，其特征在于：所述的混合交联剂为过氧化二异丙苯、氧化锌的混合物。3.根据权利要求1所述的一种大理石用防水胶，其特征在于：所述的助溶剂为纯碱。4.根据权利要求1所述的一种大理石用防水胶，其特征在于：所述的消泡剂为乳化硅油。5.利用权利要求1至4中任一项所述的一种大理石用防水胶的制造方法，其特征在于：其具体...
【专利技术属性】
技术研发人员：张明，
申请(专利权)人：无为县鑫品石业有限公司，
类型：发明
国别省市：安徽,34