The invention belongs to the technical field of materials, a weak solvent ink absorption coating and preparation method thereof, the absorption coating, the composition comprises the following raw materials in weight portion: 1 acrylic 7 copies, 8 copies, 1 Methacrylate Methacrylic acid alkyl ester twelve 3 20, 3 50 methacrylate and acrylic acid 40, 3 ethyl acrylate 3 50 copies, 70 copies of the 10 methyl methacrylate butyl methacrylate, 3 50 copies, 0.6 copies, 0.2 initiator emulsion agent, 1 5. The weak solvent ink absorbing coating prepared by the invention has good film forming performance, smooth surface, no bubbles and no cracks, good water resistance effect, good print quality, especially the ink absorption rate is excellent.
【技术实现步骤摘要】
一种弱溶剂墨水吸收涂层及其制备方法
本专利技术属于材料
，特别涉及一种弱溶剂墨水吸收涂层及其制备方法。
技术介绍
喷墨墨水按照溶剂组成大致分为水性墨水、溶剂型墨水；水性墨水无污染，但主要成分挥发速度慢，不易干燥，且画面耐候性差，主要用于室内；溶剂型墨水耐候性强，可适应户外。传统溶剂型墨水，一般为挥发速度较快的酯类和酮类有机溶剂，能够满足快速打印的要求。但其打印室内高浓度挥发性有机溶剂对室内人员的危害较大。基于以上原因弱溶剂墨水顺应而生。弱溶剂墨水又称环保型墨水，它结合了水性墨水和溶剂型墨水的优点。溶剂低挥发速度，低至微毒，对环境友好。但弱溶剂墨水中的弱溶剂挥发速度慢，故要求材质有溶剂吸收涂层。弱溶剂墨水是近几年新开发的墨水，专门针对弱溶剂墨水吸收涂层的研究极少报道，已经报道的弱溶剂墨水吸收涂层的吸墨时间长，本专利技术是一种针对弱溶剂墨水吸收涂层的开发和利用。比传统的丙烯酸乳液涂层有更快的弱溶剂墨水吸收速度，以满足弱溶剂墨水打印涂层要求。
技术实现思路
本专利技术的目的是提供一种弱溶剂墨水吸收涂层，能快速吸收吸墨弱溶剂墨水，打印效果好，画面更加清晰，且能够提高打印...
【技术保护点】
一种弱溶剂墨水吸收涂层，其组分包括以下重量份的原料：
【技术特征摘要】
1.一种弱溶剂墨水吸收涂层，其组分包括以下重量份的原料：2.根据权利要求1所述的弱溶剂墨水吸收涂层，其特征在于：所述丙烯酸和甲基丙烯酸的用量之和占组分原料总量的2-6wt％。3.根据权利要求1所述的弱溶剂墨水吸收涂层，其特征在于：所述甲基丙烯酸十二烷基酯占组分原料总量的3-6wt％。4.根据权利要求1所述的弱溶剂墨水吸收涂层，其特征在于：所述甲基丙烯酸丁酯占组分原料总量的10-14wt％。5.根据权利要求1所述的弱溶剂墨水吸收涂层，其特征在于：所述引发剂为过硫酸盐。6.根据权利要求5所述的弱溶剂墨水吸收涂层，其特征在于：所述过硫酸盐为过硫酸钾、过硫酸钠、过硫酸铵中的一种或几种的组合。7.根据权利要求1所述的弱溶剂墨水吸收涂层，其特征在于：所述乳化剂为阴离子乳化剂或/和非离子乳化剂...
【专利技术属性】
技术研发人员：夏厚君，张增辉，代树祥，潘华，
申请(专利权)人：浙江欧丽数码喷绘材料有限公司，
类型：发明
国别省市：浙江,33