The invention discloses a low temperature resistant PP R pipe and a preparation method thereof, which consists of the following parts by weight of the raw material: 50 70 PP R, 10 15 PP B, 2 3 poly butylene succinate, eggshell powder 0.5 6 copies, 2 copies of 1 6 starch, 7 block copolymer, 1 2 maleic anhydride styrene copolymer, 4 5 1 sorbitol, 2 beta crystal nucleating agent, 8 9 phthalate two formic acid methyl ester two, 1 2 formamide. The present invention by surface load beta nucleating agent modification of inorganic particles in Masterbatch, PPR pipes and joined the PP B induced crystallization preparation of high beta crystal content, compared with the prior art, the beta crystallization effect is obviously improved, which can effectively solve the low temperature brittleness of PP R pipe problems.
【技术实现步骤摘要】
一种耐低温PP-R管材及其制备方法
本专利技术涉及塑料领域，具体一种耐低温PP-R管材及其制备方法。
技术介绍
PP-R管材具有保温节能、绿色环保和优异的耐热、氧稳定性与卫生性能等优点，与其它冷热水管道相比，PP-R管道价格适中，性价比高，适合国内的市场需求。目前，我国PP-R管的推广受到几个因素的制约：(1)国产PP-R专用树脂性能不佳，原料国产程度不高。(2)PP-R管的低温韧性较差。由于耐低温冲击性能较差，在低温环境条件下，PP-R管材会发生低温脆化，因此极易在运输中损坏。
技术实现思路
本专利技术的目的在于提供一种耐低温PP-R管材及其制备方法。本专利技术的目的可以通过以下技术方案实现：一种耐低温PP-R管材，其由以下重量份数的原料制成：50-70份PP-R，10-15份PP-B，2-3份聚丁二酸丁二醇酯，蛋壳粉0.5-6份，1-2份淀粉，6-7份嵌段共聚聚丙烯，1-2份马来酸酐-苯乙烯共聚物，4-5份山梨醇，1-2份β晶型成核剂，8-9份邻苯二甲酸二甲脂，1-2份甲酰胺。优选的，所述的一种耐低温PP-R管材，其由以下重量份数的原料制成：60份PP-R，12份...
【技术保护点】
一种耐低温PP‑R管材，其特征在于，其由以下重量份数的原料制成：50‑70份PP‑R，10‑15份PP‑B，2‑3份聚丁二酸丁二醇酯，蛋壳粉0.5‑6份，1‑2份淀粉，6‑7份嵌段共聚聚丙烯，1‑2份马来酸酐‑苯乙烯共聚物，4‑5份山梨醇，1‑2份β晶型成核剂，8‑9份邻苯二甲酸二甲脂，1‑2份甲酰胺。
【技术特征摘要】
1.一种耐低温PP-R管材，其特征在于，其由以下重量份数的原料制成：50-70份PP-R，10-15份PP-B，2-3份聚丁二酸丁二醇酯，蛋壳粉0.5-6份，1-2份淀粉，6-7份嵌段共聚聚丙烯，1-2份马来酸酐-苯乙烯共聚物，4-5份山梨醇，1-2份β晶型成核剂，8-9份邻苯二甲酸二甲脂，1-2份甲酰胺。2.根据权利要求1所述的一种耐低温PP-R管材，其特征在于，其由以下重量份数的原料制成：60份PP-R，12份PP-B，3份聚丁二酸丁二醇酯，蛋壳粉3份，2份淀粉，6...