The invention discloses a composite plastic products, and relates to the technical field of plastic products, which comprises the following raw materials in parts by weight: 40 to 45 portions of polyvinyl chloride, polyolefin resin 20 ~ 30, 10 ~ 12 mulberry sawdust, NBR 8 ~ 10, 2 ~ 3 stearic acid salt, epoxy soybean oil from 3 to 5, 12 to 15 portions of plasticizer, antioxidant 2 to 3 copies, the PVC, polyolefin resin, rubber, Ding Qing stearate and epoxy soybean oil is heated to 110 to 120 DEG C, stirring for 60 to 90 minutes, then add the mulberry sawdust, plasticizer 25 ~ 40 minutes of heating and antioxidants to obtain a mixture; the mixture is injected into the mold, the mold temperature is 40 to 45 DEG C, rolled to a thickness of 0.7 ~ 1.2mm composite plastic products can solve the existing composite plastic is heated and smelly, damp moldy problem.
【技术实现步骤摘要】
复合塑料制品
本专利技术涉及塑料制品的
，尤其是一种用于汽车内饰的复合塑料制品。
技术介绍
随着社会的进步，人民的生活水平越来越高，汽车越来越多的进入了人们的生活。由于我国是个人口众多的大国，所以消费量也巨大。汽车工业发展非常快，而现在的汽车材料侧重与环保和轻量化，所以汽车内饰材料采用复合塑料为主。但是现有的汽车内饰复合塑料存在因过热而发臭，因过潮而发霉的问题。
技术实现思路
本专利技术提供一种复合塑料制品，它可以解决现有复合塑料受热发臭，受潮发霉的问题。为了解决上述技术问题，本专利技术所采用的技术方案是：这种复合塑料制品，包括以下重量份数的原料：聚氯乙稀40～45份，聚烯烃树脂20～30份，桑木屑10～12份，丁晴橡胶8～10份，硬脂酸盐2～3份，环氧大豆油3～5份，增塑剂12～15份，抗氧剂2～3份。上述复合塑料制品，它的制作方法包括以下步骤：1）将所述聚氯乙稀、聚烯烃树脂、丁晴橡胶、硬脂酸盐和环氧大豆油加热至110～120℃搅拌60～90分钟后，然后加入所述桑木屑、增塑剂和抗氧剂加热25～40分钟得到混合料；2）将步骤1）所得混合料注入模具中，所述模具温度...
【技术保护点】
一种复合塑料制品，其特征在于包括以下重量份数的原料：聚氯乙稀40～45份，聚烯烃树脂20～30份，桑木屑10～12份，丁晴橡胶8～10份，硬脂酸盐2～3份，环氧大豆油3～5份，增塑剂12～15份，抗氧剂2～3份；其制作方法包括以下步骤：1）将所述聚氯乙稀、聚烯烃树脂、丁晴橡胶、硬脂酸盐和环氧大豆油加热至110～120℃搅拌60～90分钟后，然后加入所述桑木屑、增塑剂和抗氧剂加热25～40分钟得到混合料；2）将步骤1）所得混合料注入模具中，所述模具温度为40～45℃，辊压成厚度为0.7～1.2mm的复合塑料制品即可。
【技术特征摘要】
1.一种复合塑料制品，其特征在于包括以下重量份数的原料：聚氯乙稀40～45份，聚烯烃树脂20～30份，桑木屑10～12份，丁晴橡胶8～10份，硬脂酸盐2～3份，环氧大豆油3～5份，增塑剂12～15份，抗氧剂2～3份；其制作方法包括以下步骤：1）将所述聚氯乙稀、聚...