The invention belongs to the field of building materials, in particular to a efflorescence wall with energy-saving insulation board and preparation method, according to the percentage of the total weight of raw material, consists of the following raw materials: glass beads of 73 76%, water soluble adhesive 18 30%, 3 5% hydrophobic agent, its preparation method includes the following the following steps: A, glass beads, water soluble adhesive and water repellent is added into the mixer mixing, to obtain a mixture; B, the mixture obtained in step A to the mold, through forming hydraulic press pressing sheet; C, plate can be obtained in step B by micro wave drying and curing, obtain energy-saving insulation plate, compared with the prior art, the invention of energy-saving insulation plate can effectively solve the wall efflorescence phenomenon, at the same time with fire prevention, heat preservation function, the preparation method is simple.
【技术实现步骤摘要】
一种不泛碱墙面用保温节能板及制备方法
本专利技术属于建筑材料领域，尤其涉及一种不泛碱墙面用保温节能板及制备方法。
技术介绍
在现代建筑行业，建筑物的墙面随着时间的推移，易出现泛碱的现象，泛碱是指一般家庭建筑或工程建筑使用的硅酸盐混凝土，在经过一段时间后，墙面会出现盐霜似的晶体。毛坯房会直接析出，装潢过的，涂料油漆等会鼓起、起皮、脱落。长年不褪，严重影响外观，此种现象称为"泛碱"现象，同时目前墙面还不具有防火性和节能保温功能。
技术实现思路
本专利技术为了解决上述技术问题提供一种可有效的解决墙面泛碱的现象，同时使墙面具有防火、保温的保温节能板，其制备方法简单。本专利技术解决上述技术问题的技术方案如下：一种不泛碱墙面用保温节能板，按原料总重量的百分含量计，由如下原料组成：玻化微珠73-76％，水溶性粘接剂18-30％，憎水剂3-5％。本专利技术的有益效果是：本专利技术保温节能板材可有效的解决墙面泛碱的现象，同时具有防火、保温功能，其制备方法简单。在上述技术方案的基础上，本专利技术还可以做如下改进。作为本专利技术进一步优选，所述水溶性粘接剂为萜烯树脂、酚醛树脂、丙烯酸树脂中...
【技术保护点】
一种不泛碱墙面用保温节能板，其特征在于，按原料总重量的百分含量计，由如下原料组成：玻化微珠73‑76％，水溶性粘接剂18‑30％，憎水剂3‑5％。
【技术特征摘要】
1.一种不泛碱墙面用保温节能板，其特征在于，按原料总重量的百分含量计，由如下原料组成：玻化微珠73-76％，水溶性粘接剂18-30％，憎水剂3-5％。2.根据权利要求1所述一种不泛碱墙面用保温节能板，其特征在于，所述水溶性粘接剂为萜烯树脂、酚醛树脂、丙烯酸树脂中的一种或几种的混合物，所述憎水剂为硅系憎水剂。3.根据权利要求1所述一种不泛碱墙面用保温节能板，其特征在于，所述玻化微珠粒径为100-200目。4.一种不泛碱墙面用保温节能板的制备方法，其特征在于，包括以下步骤：A、将玻化微珠、水溶性粘接剂和憎水剂加入搅拌机中混合均匀，得到混合物；B、将步骤A中...