The invention provides a high viscosity color cement modified materials, cement modified asphalt and preparation method, including: cement components and anti stripping components, the cement components include matrix cementation component, polymer fiber and thickening agent, on this basis, adding organic toner, can change pavement color, further reduce the absorption of solar radiation. The high viscosity color cementing modified material, the cemented Modified mixture and the preparation method of the invention can effectively reduce the pavement temperature and improve the safety of pavement use, and the preparation method is simple and the cost is low.
【技术实现步骤摘要】
一种高黏彩色胶结改性材料、胶结改性混合料及制备方法
本专利技术涉及道路及建筑材料，更具体地，涉及一种高黏彩色胶结改性材料、胶结改性混合料及制备方法。
技术介绍
道路路面大多为黑色路面(沥青路面)和白色路面(水泥路面)两种。单调的色彩使得其与周边环境的协调性较差，容易导致驾驶员的疲倦感，不利于营造一个舒适而安全的行车环境。同时，由于沥青路面和水泥混凝土路面极强的传热性也给城市带来了“热岛效应”，城市道路白天积聚的热量夜晚难以消散，致使城市平均温度升高。高温天气、高温路面、高温疾病一步步侵蚀着城市的居民，据新闻报道，城市热岛强度最大已达7℃，高温疾病死亡率提高31.2％，交通事故率增加27.7％。控制城市热岛的继续发展已经是迫在眉睫的事情，城市温度升高，直接导致气压降低带来污染物聚集问题、城市居民受到高温疾病的概率增大、路用性能也极大地降低。随着城市化进程加快，城市中原有土壤表面逐步被房屋、大型基础设施及各种不透水的场地和道路所取代。城市道路多采用平整度高、舒适性好、噪音低的沥青路面形式。国内外的研究表明，当气温达到35℃时，沥青路表温度可达到60～65℃，造成了严重...
【技术保护点】
一种胶结改性材料，其特征在于，包括：胶结组分和抗剥落组分，所述胶结组分包括基质胶结组分、高分子纤维和增稠剂。
【技术特征摘要】
1.一种胶结改性材料，其特征在于，包括：胶结组分和抗剥落组分，所述胶结组分包括基质胶结组分、高分子纤维和增稠剂。2.如权利要求1所述的一种胶结改性材料，其特征在于，所述基质胶结组分具体为：脂肪族树脂、脂环族树脂、芳香族树脂、脂肪族/芳香族共聚树脂和加氢石油树脂中的一种或者几种。3.如权利要求1或2所述的一种胶结改性材料，其特征在于：所述基质胶结组分在所述胶结组分中的质量百分比为65％-80％，所述高分子纤维在所述胶结组分中的质量百分比为5％-10％，所述增稠剂在所述胶结组分中的质量百分比为10％-30％；优选地，所述基质胶结组分在所述胶结组分中的质量百分比为65％-75％，所述高分子纤维在所述胶结组分中的质量百分比为7％-10％，所述增稠剂在所述胶结组分中的质量百分比为18％-25％。4.如权利要求1-3任一项所述的一种胶结改性材料，其特征在于，所述抗剥落组分为：木质素磺酸钙、木质素磺酸钠和石油树脂中的一种或者几种。5.如权利要求1-4任一项所述的一种胶结改性材料，其特征在于：所述胶结组分的质量百分比为50％-90％、所述抗剥落组分的质量百分比为10％-50％；优选地，所述胶结组分的质量百分比为70％-90％、所述抗剥落组分的质量百分比为10％-30％；优选地，所述胶结组分的质量百分比为80％-90％、所述抗剥落组分的质量百分比为10％-20％。6.如权利要求1-5任一项所述...
【专利技术属性】
技术研发人员：索智，季节，金珊珊，郭峰，张奥，谢聪聪，
申请(专利权)人：北京建筑大学，
类型：发明
国别省市：北京,11
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。