The invention provides a limestone mineral composite material, made by weight of raw materials, lime stone 30 80 copies, 30 copies, 10 slag magnesia powder 5 10 copies, 8 copies, 3 nitrate gypsum powder 20 50 and 5 triethanolamine 15. The composite material can improve the concrete early and late strength of lime stone powder to promote early hydration of cement, at the same time, triethanolamine also had a beneficial effect on the development of concrete strength; to improve the durability of concrete and limestone powder admixture can effectively reduce the concrete porosity, the pore structure refinement, improved the pore structure, can effectively reduce the chloride ion diffusion coefficient of concrete, and the hydration products of triethanolamine dense structure of cement. The preparation process is simple, the cost is low, and it is suitable for large-scale industrial production.
【技术实现步骤摘要】
一种石灰石粉矿物复合料
本专利技术属于石灰石
，具体涉及一种石灰石粉矿物复合料。
技术介绍
石灰石是一种主要由方解石(CaCO3)组成的矿物，其天然资源丰富，分布广泛，容易获得。作为水泥生产原料和混凝土的粗、细骨料，在开采石灰石和生产机制砂、石的过中不可避免的产生了大量的石灰石粉，如果将其废弃必将形成巨大的环境污染，增加环负荷，占用土地。因此，若能利用石灰石粉作掺合料减少水泥用量，达到提高混凝土拌和物性能和强度，改善混凝土的耐久性能，这不仅能弥补现有掺合料稀缺和不足，还能降低生产成本，减少废气排放，减轻环境负荷，对循环经济产生积极的影响。我国是水泥生产和混凝土应用大国，大规模的基础设施建设正在持续进行，使石灰石粉得到科学、合理的利用，同时产生良好的技术、经济和生态效益是非常有现实意义的。许多研究表明，一定细度的石灰石粉，当其掺量在10％以内时可以提高水泥石的早期强度，随着掺量继续增加，则会明显降低水泥强度。因此，石灰石粉在水泥混凝土中的掺量难以提高，限制了它的广泛应用，使混凝土后期强度增长慢更加制约了石灰石粉在水泥混凝土中的应用。本专利技术旨在克服现有石灰石...
【技术保护点】
一种石灰石粉矿物复合料，其特征在于，由以下重量份原料制成，石灰石粉30‑80份、矿渣粉10‑30份、氧化镁粉5‑10份、硝酸盐3‑8份、石膏粉20‑50份和三乙醇胺5‑15份。
【技术特征摘要】
1.一种石灰石粉矿物复合料，其特征在于，由以下重量份原料制成，石灰石粉30-80份、矿渣粉10-30份、氧化镁粉5-10份、硝酸盐3-8份、石膏粉20-50份和三乙醇胺5-15份。2.根据权利要求1所述的一种石灰石粉矿物复合料，其特征在于：所述的石灰石粉为生产机制砂所产生的细屑经粉磨至勃氏比表面积为200-300m2/kg的干粉。3.根据权利要求1所述的改性一种石灰石粉矿物复合料，其特征在于：所述的矿渣粉是冶炼生铁时排出的熔融渣，经粉磨后得到的勃氏比表面积为300-400m2/kg，7天活性指...
【专利技术属性】
技术研发人员：陈永忠，
申请(专利权)人：青阳县永诚钙业有限责任公司，
类型：发明
国别省市：安徽,34