利用菌糠生产无胶纤维板的方法技术

本发明专利技术提供了一种利用菌糠生产无胶纤维板的方法，以菌糠为原料，再添加一定秸秆后进行生物改性，进一步通过温控改性后并进行热压，实现无胶纤维板的制备。本发明专利技术的纤维板制备中不添加化学胶黏剂，有效利用了菌糠及秸秆等废弃物，解决了当前纤维板存在的环境污染、成本高等问题，是一种绿色可持续发展的纤维板制备方法。

The method of producing non gel fiberboard by using bacterial bran

The invention provides a method for producing non adhesive fiberboard by using mushroom chaff, taking biological chaff as raw material and adding certain straw after biological modification, and further through temperature control modification and hot pressing, so as to achieve the preparation of non adhesive fiberboard. The preparation of fiberboard in the invention does not add chemical adhesives, effectively utilizes such wastes as mushroom bran and straw, and solves the problems of environmental pollution and high cost existing in fiberboard, and is a green and sustainable development method for fiberboard.

【技术实现步骤摘要】
利用菌糠生产无胶纤维板的方法
本专利技术涉及纤维板的制备方法，特别是涉及通过菌糠生物改性及酶法处理生产无胶纤维板的方法。
技术介绍
据统计，我国已成为世界人造纤维板生产和消费第一大国，产值超千亿元。尽管我国人造纤维板产量不断增加，但仍然无法满足市场需求，同时原料供应也存在严重的不足。在纤维板制造过程中通常需添加一些醛类胶黏剂，如脲醛树脂胶、酚醛树脂胶、三聚氰胺甲醛树脂胶等，这些醛类胶黏剂的使用，将导致：1）纤维板生产和使用过程中释放甲醛，面临环保和健康压力；2）以不可再生资源——石油合成胶黏剂，与能源争油。近年来，基于绿色家居考虑，无甲醛胶黏剂型和无胶黏剂型环保型纤维板生产技术已成为了研究的热点，无胶纤维板更是成为市场热宠。菌糠是利用秸秆、木屑等原料进行食药用菌代料栽培，收获后的培养基剩余物，俗称栽培废料、菌渣或余料，是食用菌丝残体及经食用菌酶解，结构发生质变的粗纤维等成分的复合物。因此，菌糠较之秸秆、木屑等原料具有更高含量的粗蛋白、粗脂肪、多糖、有机酸等有机物，另外，纤维素、半纤维素和木质素等组分也发生了不同程度的降解与改性，出现了断裂及多孔性状。另外，新鲜菌糠中扔残留有高活性的木本文档来自技高网...

【技术保护点】
利用菌糠生产无胶纤维板的方法，其特征在于该纤维板的生产方法包括以下步骤：（1）选取新鲜菌糠，打散，添加秸秆粉，制备成菌糠培养基，菌糠培养基不用灭菌处理；（2）对菌糠培养基进行生物改性，获改性菌糠；（3）改性菌糠恒温处理实现菌糠的自我酶改性；（4）自我酶改性处理后的菌糠通过热压工艺，制备得纤维板。

【技术特征摘要】
1.利用菌糠生产无胶纤维板的方法，其特征在于该纤维板的生产方法包括以下步骤：（1）选取新鲜菌糠，打散，添加秸秆粉，制备成菌糠培养基，菌糠培养基不用灭菌处理；（2）对菌糠培养基进行生物改性，获改性菌糠；（3）改性菌糠恒温处理实现菌糠的自我酶改性；（4）自我酶改性处理后的菌糠通过热压工艺，制备得纤维板。2.如权利要求1所述的利用菌糠生产无胶纤维板的方法，其特征在于：所述的菌糠包括食用菌糠、药用菌糠。3.如权利要求1所述的利用菌糠生产无胶纤维板的方法，其特征在于：所述的秸秆包括小麦秸秆、玉米秸秆、高粱秸秆、芦苇、油菜秸秆、蓖麻秸秆、红薯藤、南瓜藤、丝瓜藤。4.如权利要求1所述的利用菌糠生产无胶纤维板的方法，其特征在于：菌糠培养...

【专利技术属性】
技术研发人员：邬建国，梁小华，王新风，纪丽莲，张曈，夏林，陆家锦，吴蕾蕾，陈春燕，
申请(专利权)人：淮阴师范学院，
类型：发明
国别省市：江苏,32