The invention relates to a small splash of solid wire, calculated according to the weight percentage, which comprises the following raw materials: C = 0.15%, Mn:0.30 ~ 0.6%, Si = 0.30 ~ 0.50%, Cr = 0.20%, Ni = 0.25 ~ 0.45%, Cu = 0.20%, S:0.015 ~ 0.030%, P = 0.030, B = Ti:0.02 ~ 0.062%. 0.0008%, O:0.0010 - 0.0045%, P = 0.025%, the balance of iron and unavoidable impurities. This invention by adjusting the chemical composition of solid wire formulation design, its stability and improve the mechanical properties of weld, welding spatter, weld forming, welding wire side top board welding performance defects, forming beautiful, solve the problem of slow wire melting speed.
【技术实现步骤摘要】
一种飞溅小的实心焊丝
本专利技术涉及一种焊丝,具体是涉及一种飞溅小的实心焊丝。
技术介绍
随着微合金化技术的开发和冶金工艺技术的进步,耐大气腐蚀钢配套焊接材料的开发使用始终处于一种增长的趋势,作为其连接主要手段的焊接来说,其配套的焊接材料的研发生产也越来越显得尤为急迫和重要。随着科学技术的发展,更高耐蚀要求的钢板需要更高级别的焊丝来匹配。然而,现有的实心焊丝与上述高耐蚀型耐候钢钢板进行焊接时其焊缝抗拉强度太高,力学性能不稳定,且其工艺性能缺点较为明显,主要体现为焊接飞溅大、焊缝成型不良等缺陷。
技术实现思路
本专利技术要解决的技术问题是克服现有技术焊接飞溅大、焊缝成型不良的缺陷,提供一种飞溅小的实心焊丝。为解决上述技术问题,本专利技术提供以下技术方案:一种飞溅小的实心焊丝,按照重量百分比数计算,包括以下原料制成:C≤0.15%,Mn:0.30~0.6%,Si≤0.30~0.50%,Cr≤0.20%,Ni≤0.25~0.45%,Cu≤0.20%,S:0.015~0.030%,P≤0.030,Ti:0.02~0.062%,B≤0.0008%,O:0.0010~0.0045%,P≤0.025%,余量为铁和不可避免的杂质。进一步的,所用的C的含量为0.11~0.15wt%。进一步的,所用的P的含量为0.0250wt%。进一步的,所用的Ni的含量为0.35~0.40wt%。本专利技术与现有技术相比具有的有益效果是:一种飞溅小的实心焊丝,通过调整实心焊丝化学成分配方设计,稳定其焊缝力学性能,并改善其焊接飞溅大、焊缝成型不良、焊接过程中焊丝顶板子等焊接工艺性能缺点,成型美观 ...
【技术保护点】
一种飞溅小的实心焊丝,其特征在于:按照重量百分比数计算,包括以下原料制成:C≤0.15%,Mn:0.30~0.6%,Si≤0.30~0.50%,Cr≤0.20%,Ni≤0.25~0.45%,Cu≤0.20%,S:0.015~0.030%,P≤0.030,Ti:0.02~0.062%,B≤0.0008%,O:0.0010~0.0045%,P≤0.025%,余量为铁和不可避免的杂质。
【技术特征摘要】
1.一种飞溅小的实心焊丝,其特征在于:按照重量百分比数计算,包括以下原料制成:C≤0.15%,Mn:0.30~0.6%,Si≤0.30~0.50%,Cr≤0.20%,Ni≤0.25~0.45%,Cu≤0.20%,S:0.015~0.030%,P≤0.030,Ti:0.02~0.062%,B≤0.0008%,O:0.0010~0.0045%...