The invention relates to the celadon formula, especially a kind of dark colored and colorful glaze. A beautiful black porcelain glaze in the present invention, including porcelain and glaze layer, by weight percentage, the blank prepared by the new porcelain clay 33%, high head check purple soil 28%, under 8% and Jin Tan family Zijin clay clay 31% denier composition; the preparation of enamel glaze by 35 40% Mu Dai glaze soil and stone Xuanhu quartz powder 3 8%, lion ridge 25%, 20 Zijin clay limestone Qingyuan 10 15%, 12%, 10 lithium feldspar talcum powder 15 18%, 4% and 5 borax 2 iron 9%. The beneficial effect of the invention is: it is good to restore the beautiful and beautiful color of the Song Dynasty, and it is beautiful and generous.
【技术实现步骤摘要】
一种宋瓷玄色斑斓釉及其制备方法
本专利技术涉及青瓷配方，尤其是一种玄色斑斓釉。本专利技术涉及青瓷加工工艺，尤其是一种玄色斑斓釉制备方法。
技术介绍
中国是瓷器的故乡，瓷器的专利技术是中国对世界文明的伟大贡献，在英文中"瓷器"(china）一词已成为"中国"的代名词。大约在公元前16世纪的商代中期，中国就出现了早期的瓷器。龙泉青瓷是非常具有中国特色传统瓷器珍品，南北朝时期，浙江龙泉人利用当地优越的自然条件，制造青瓷。早在南宋时龙泉就烧制出晶莹如玉的粉青釉和梅子青釉，使龙泉青瓷达到颠峰。青如玉、明如镜、薄如纸、声如磬。龙泉市烧制青瓷的古代窑址有500多处，龙泉市境内有360多处，史称龙泉窑。龙泉青瓷的传承和创新必须把握好两点：一是牢牢把握龙泉青瓷的灵魂：不仅仅是指龙泉青瓷温润如玉的釉色，更是其典雅高贵的气质。二是在器形上创新它。这就必须从南宋着手，因为南宋王朝偏安一隅，其瓷器风格是精致有余而大气不足（但南宋的可贵之处是给人们以思想的自由，所以南宋创造了中国文化之高峰）。因而可以借鉴中国古代的文化元素，如黄河彩窑、商周青铜器、汉罐等等古朴大气的风格，当然也应该揉入制作者...
【技术保护点】
一种宋瓷玄色斑斓釉，包括瓷胎和釉层，其特征在于，以重量百分数计，所述制备瓷胎的坯料由新查瓷土33%、高际头紫金土28%、下潭户紫金土8%和锦旦瓷土31%组成；所述制备釉层的釉料由木岱釉土 35‑40%、石玄湖石英粉3‑8%、狮子垄紫金土 20‑25%、庆元石灰石10‑15%、锂长石10‑12%、滑石粉15‑18%、硼砂2‑4%和铁衣5‑9%组成。
【技术特征摘要】
1.一种宋瓷玄色斑斓釉，包括瓷胎和釉层，其特征在于，以重量百分数计，所述制备瓷胎的坯料由新查瓷土33%、高际头紫金土28%、下潭户紫金土8%和锦旦瓷土31%组成；所述制备釉层的釉料由木岱釉土35-40%、石玄湖石英粉3-8%、狮子垄紫金土20-25%、庆元石灰石10-15%、锂长石10-12%、滑石粉15-18%、硼砂2-4%和铁衣5-9%组成。2.根据权利要求1所述的一种宋瓷玄色斑斓釉，其特征在于，瓷胎:釉料:水重量比例为1.8：1：0.8。3.一种宋瓷玄色斑斓釉的制备方法，包括如下步骤：制备宋瓷玄色斑斓釉料，将所述各釉料组分：釉料由木岱釉土35-40%、石玄湖石英粉3-8%、狮子垄紫金土20-25%、庆元石灰石10-15%、锂长石10-12%、滑石粉15-18%、硼砂2-4%和铁衣（四氧化三铁）5-9%进行混合均匀，并以球石:釉料:水比例为1.8：1：0.8，装入球磨设备经过30-35小时的球磨成细度为200-300目，过滤除铁；制备青瓷坯泥，坯料组分：新查瓷土33%、高际头紫金土28%、下潭户紫金土8%和锦旦瓷土31%组成，经过选矿、粉碎、配料、淘漂、加水搅拌、过滤除铁...