本发明专利技术公开了一种多功能纺织面料，其特征在于：所述多功能面料基于普通面料的基础上涂覆了特殊涂层，所述特殊涂层包括热熔胶、纳米二氧化钛粉末、纳米抗菌粉末、纳米红外粉末组成；本发明专利技术的优点在于：本发明专利技术通过在涂层中添加了二氧化钛活性材料，涂胶干燥后形成薄膜，在光线的作用下，可以产生强烈催化降解功能；能够有效的降解空气中的有害气体，能够有效杀害多种细菌，同时还具备除臭、抗污功能。

A multifunctional textile fabric

The invention discloses a multifunctional textile fabric, which is characterized in that the multifunctional fabric based on ordinary fabric coated with a special coating, the special coating including hot melt adhesive, nano titanium dioxide powder, nano antibacterial powder, nano infrared powder composition; the present invention has the advantages that the invention by adding titanium dioxide the active material in the coating, coating film formed after drying, in light of the role, can produce a strong catalytic degradation function; can be effective in the degradation of air harmful gases, can effectively kill a variety of bacteria, but also has the function of deodorization, anti fouling.

【技术实现步骤摘要】
一种多功能纺织面料
本专利技术涉及纺织
，具体涉及一种多功能纺织面料。
技术介绍
随着时代的发展，人们对于纺织面料的要求已经不局限于保暖，更多的是追求面料的功能属性，但是，现有的市场上流通的纺织面料的功能性较为单一，无法满足人们的需求。
技术实现思路
本专利技术的目的在于针对现有技术的不足，现提供一种具有抗菌、防霉和防辐射功能于一身的多功能纺织面料。为实现上述目的，本专利技术的技术方案是：一种多功能纺织面料，其创新点在于：所述多功能面料基于普通面料的基础上涂覆了特殊涂层，所述特殊涂层包括热熔胶、纳米二氧化钛粉末、纳米抗菌粉末、纳米红外粉末和纳米吸波材料粉末组成；所述热熔胶含量100-200份、纳米二氧化钛粉末含量为10-14份、纳米抗菌粉末30-60份和纳米红外粉末2-6份。进一步的，所述纳米二氧化钛粉末、纳米抗菌粉末、纳米红外粉末的颗粒直径为10-25nm。进一步的，所述特殊涂层的加工方法为：将上述质量比例的热熔胶、纳米二氧化钛粉末、纳米抗菌粉末、纳米红外粉末放入离心混合机中进行高速离心作用，所述速度为13000-15000rpm,然后加入纯净水，所述纯净水的质量为完全将混合粉末本文档来自技高网...

【技术保护点】
一种多功能纺织面料，其特征在于：所述多功能面料基于普通面料的基础上涂覆了特殊涂层，所述特殊涂层包括热熔胶、纳米二氧化钛粉末、纳米抗菌粉末、纳米红外粉末和纳米吸波材料粉末组成；所述热熔胶含量100‑200份、纳米二氧化钛粉末含量为10‑14份、纳米抗菌粉末30‑60份和纳米红外粉末2‑6份。

【技术特征摘要】
1.一种多功能纺织面料，其特征在于：所述多功能面料基于普通面料的基础上涂覆了特殊涂层，所述特殊涂层包括热熔胶、纳米二氧化钛粉末、纳米抗菌粉末、纳米红外粉末和纳米吸波材料粉末组成；所述热熔胶含量100-200份、纳米二氧化钛粉末含量为10-14份、纳米抗菌粉末30-60份和纳米红外粉末2-6份。2.根据权利要求1所述的一种多功能纺织面料，其特征在于：所述纳米二氧化钛粉末、纳...