一种波纹复合纱及其加工工艺制造技术

本发明专利技术涉及一种波纹复合纱及其加工工艺，其中所述的波纹复合纱包括纤维基料，所述的纤维基料包含有不锈钢长丝、棉、羊毛和麻组成，其中质量比为不锈钢长丝2％‑4％、棉35％‑55％、羊毛18％‑30％、麻11％‑45％。本发明专利技术采用牦牛绒单纱和聚丙烯腈纤维单纱作为主要原料，赋予混纺波纹纱冗长细致的外观，绒毛质感柔顺，保暖性好，而且具有抗静电性能，不易吸附灰尘，易于维护，耐脏性好。

Corrugated composite yarn and its processing technology

The invention relates to a corrugated composite yarn and its processing technology, including corrugated composite yarn comprises a fiber base material, fiber base material comprising a stainless steel filament, cotton, wool and flax, the mass ratio of 2% 4% stainless steel filament, cotton, wool 35% 55% 18% 30%, 11% Ma 45%. The present invention adopts yak cashmere single yarn and polyacrylonitrile fiber single yarn as main raw materials, gives the blended ripple yarn long and detailed appearance, has downy texture, good thermal insulation property, and has antistatic performance, and is not easy to adsorb dust, easy to maintain, good dirt resistance.

【技术实现步骤摘要】
一种波纹复合纱及其加工工艺
本专利技术属于一种纱的制造工艺，具体涉及一种波纹复合纱及其加工工艺。
技术介绍
当今社会，纺织服装业处于一个追求时尚，多元和高品质的时期，近年来，波纹纱是一种非常规的纱线，由于表面的绒毛质感丰富，主要应用在毛衣以及风衣等服饰领域，手感温暖细腻，制成的面料防风性好，保暖性强，在女性服饰领域应用的较多。由于波纹纱的表面绒毛细腻，因此比较容易吸附灰尘，灰尘颗粒物附着在波纹纱制成的衣物上，除了水洗，一般情况下难以清除，影响衣物的质感，客户满意度差。
技术实现思路
本专利技术所要解决的技术问题是，针对以上现有技术存在的缺点，提出一种操作简单，生产效率高的一种波纹复合纱及其加工工艺，该制造工艺生产出来的波纹复合纱牢度强，耐磨，花式多，且手感好。本专利技术所采用的技术方案是：一种波纹复合纱，包括纤维基料，所述的纤维基料包含有不锈钢长丝、棉、羊毛和麻组成，其中质量比为不锈钢长丝2％—4％、棉35％-55％、羊毛18％-30％、麻11％-45％。一种波纹复合纱的加工工艺，包括以下步骤：(1)、将选好后的纤维进行拉伸；(2)、将拉伸后的纤维与不绣钢长丝进行交织；(3)、按照规定的本文档来自技高网...

【技术保护点】
一种波纹复合纱，其特征在于：包括纤维基料，所述的纤维基料包含有不锈钢长丝、棉、羊毛和麻组成，其中质量比为不锈钢长丝2％‑4％、棉35％‑55％、羊毛18％‑30％、麻11％‑45％。

【技术特征摘要】
1.一种波纹复合纱，其特征在于：包括纤维基料，所述的纤维基料包含有不锈钢长丝、棉、羊毛和麻组成，其中质量比为不锈钢长丝2％-4％、棉35％-55％、羊毛18％-30％、麻11％-45％。2.一种波纹复合纱的加工工艺，其特征在于：包括以下步骤：(1)、将选好后的纤维进行拉伸；(2)、将拉伸后的纤维与不绣钢长丝进行交织；(3)、按照规定的重量，将筵棉均匀、稳定地通过成卷机喂入梳棉机；(4)...

【专利技术属性】
技术研发人员：王沛龙，
申请(专利权)人：句容市润龙纺织品有限公司，
类型：发明
国别省市：江苏,32