The invention discloses a processing technique of a long-acting antibacterial polyester filament, which comprises the following steps: A, the thermoplastic polyurethane slice after cleaning drying and antibacterial agent mixed with screw extrusion by melting and mixing machine; B, in the extruder metering section or in extruder, into the mixer before joining crosslinking agent; C, melt spun material through a spinneret plate, spinning and winding, and finally get the finished product. The production process is as follows: slice cleaning drying extrusion mixing spray wire drawing cooling oil oiling winding. The antibacterial agent is silver powder and silver powder is nanometer silver powder. The invention has the advantages of simple production, high production efficiency, low investment, good antibacterial property, strong antibacterial durability, stable quality and easy popularization.
【技术实现步骤摘要】
一种长效抗菌涤纶长丝的加工工艺
本专利技术涉及化纤加工
，尤其是一种长效抗菌涤纶长丝的加工工艺。
技术介绍
化纤分为很多种涤纶是其中比较常见的一种，涤纶的生产技术可分为4种：干纺、湿纺、反应纺和熔纺。不论是使用何种纺丝工艺，所生产出的化学纤维性质基本上完全相同，多为白色长丝，横截面形状根据生产工艺的不同存在一定差异。干纺涤纶长丝多为圆型、椭圆型级哑铃型横截面；湿纺及化学纺涤纶长丝主要为粗大的叶型及不规则截面没并且各丝条之间犹豫发生熔接而在其纵向形成不规则的粘接点，由此形成粘接复丝束；熔纺涤纶主要为圆型截面的单丝或复丝。干纺是目前世界上应用最广泛的涤纶纺丝方法，产量约为世界涤纶总产量的80％。干纺工艺技术成熟，制成的纤维质量和性能都很优良，但技术难度较大，需溶剂回收，生产成本相对较高。湿纺与反应纺工艺复杂，装置设备投资费用大，纺丝速度较低，生产成本高，该法基本已经被淘汰，熔纺是近年发展起来的制造涤纶的新方法，具有干纺和反应纺的优点，并且工艺流程简单、设备投入低、生产效率高，纺速一般可达到400-800m/min，在生产过程中无需使用溶剂，是最为经济和对环境最为有益的涤纶生产技术。运用熔纺涤纶技术，任何生产商都可以自行生产涤纶，颜色、添加剂及纤维直径可任意选择。目前市面上的涤纶比较普通，现在细菌的种类越来越多，普通的涤纶不具备抗菌功能，不能满足现代人们的需求，因此急需一种改进的技术来解决上述技术缺陷。
技术实现思路
本专利技术提供了一种长效抗菌涤纶长丝的加工工艺。本专利技术针对上述技术缺陷所提出的技术方案是：一种长效抗菌涤纶长丝的加工工艺，包括以下步骤：a、...
【技术保护点】
一种长效抗菌涤纶长丝的加工工艺，其特征在于：包括以下步骤：a、把热塑性聚氨酯切片经清洗干燥后与抗菌剂混合加入螺杆挤出机中进行熔融、混炼；b、在挤出机的计量段或在挤出机后、进入混合器前加入交联剂；c、熔纺物料经喷丝板喷出、纺丝和卷绕成型，最后得到成品。
【技术特征摘要】
1.一种长效抗菌涤纶长丝的加工工艺，其特征在于：包括以下步骤：a、把热塑性聚氨酯切片经清洗干燥后与抗菌剂混合加入螺杆挤出机中进行熔融、混炼；b、在挤出机的计量段或在挤出机后、进入混合器前加入交联剂；c、熔纺物料经喷丝板喷出、纺丝和卷绕成型，最后得到成品...