The present invention relates to a water-based damping coating and a preparation method thereof, according to the weight calculation, which comprises the following raw materials: silicone acrylic emulsion 40 - 60, 20 - 30, polyvinyl alcohol emulsion polyvinyl acetate emulsion was 20 ~ 30, 50 ~ 70 functional filler and flame retardant in 2 ~ 6, preservatives 1 - 3, leveling agent 1 - 3, coalescents 2 ~ 6, 0.5 ~ 2 thickening agent and deionized water from 30 to 60. The damping coating has the advantages of environmental protection, no toxicity, moderate viscosity, easy construction, wide temperature range of viscoelastic state, good mechanical property and good blending property.
【技术实现步骤摘要】
水性阻尼涂料及其制备方法
本专利技术属于阻尼涂料
，具体涉及一种阻尼系数高的水性阻尼涂料及其制备方法。
技术介绍
目前国内外阻尼涂料种类较多，但从涂料的溶剂来分主要有溶剂型和水性型两种。前者大多含有机溶剂及沥青，毒性高、挥发性大、污染环境、施工性差，现已较少使用。后者阻尼涂料以水为溶剂，具有低毒低气味、低成本、易施工、环保性，是城轨车辆用阻尼涂料的首选产品。水性涂料以水为分散介质无毒环保，以高性能树脂为成膜物，以无机物为填料，性能优异，施工方便。现已广泛应用于机车火箭、工程机械、家用电器等。随着现代工业、交通运输、宇航事业的发展以及对环境保护的重视，阻尼材料必然日益需要，尤其是高性能环保型的阻尼材料。目前的阻尼涂料很难满足使用要求，主要存在以下缺点：有机溶剂型阻尼料，存在有机溶剂挥发污染环境的问题；水性阻尼涂料阻尼性能较低，阻尼温域较窄；阻燃性能有待提高。
技术实现思路
本专利技术提出一种水性阻尼涂料，该阻尼涂料环保无毒，粘稠度中等易于施工，拓宽了材料的粘弹态温域范围，并且力学性能好，共混性好。本专利技术的技术方案是这样实现的：一种水性阻尼涂料，按重量份数计算，...
【技术保护点】
一种水性阻尼涂料，其特征在于，按重量份数计算，包括以下原料：硅丙乳液40～60份、聚乙烯醇乳液20～30份、聚醋酸乙烯乳液20～30份、功能填料50～70份、阻燃剂2～6份、防腐剂1～3份、流平剂1～3份、成膜助剂2～6份、增稠剂0.5～2份以及去离子水30～60份。
【技术特征摘要】
1.一种水性阻尼涂料，其特征在于，按重量份数计算，包括以下原料：硅丙乳液40～60份、聚乙烯醇乳液20～30份、聚醋酸乙烯乳液20～30份、功能填料50～70份、阻燃剂2～6份、防腐剂1～3份、流平剂1～3份、成膜助剂2～6份、增稠剂0.5～2份以及去离子水30～60份。2.根据权利要求1所述的水性阻尼涂料，其特征在于，所述功能填料为纳米蒙脱土、鳞片石墨、粗海泡石与滑石粉的混合物。3.根据权利要求2所述的水性阻尼涂料，其特征在于，纳米蒙脱土、鳞片石墨、粗海泡石与滑石粉的质量比为7～9:5～6:2～4:3～5...
【专利技术属性】
技术研发人员：汪琦，汪泽维，
申请(专利权)人：合肥泓定科技有限公司，
类型：发明
国别省市：安徽,34