一种油漆制造技术

本发明专利技术涉及一种油漆，其特征在于：由以下按照重量份的原料组成：油漆组分30‑50份，沸石粉10‑20份，松香树脂8‑13份，钛白粉15‑20份、聚乙烯醇缩丁醛5‑10份，不浮型铝粉浆液1‑5份，磷酸3‑7份，水40‑50份、羟乙基纤维素8‑10份，滑石粉4‑6份，碱式氯化铋1‑2份，水溶树脂2‑4份，丁醇5‑7份，硬脂酸丁酯7‑9份，石油1‑2份；原料主要为一些市场上常见的材料，容易取得，并且成本不高；本发明专利技术的加入了磷酸和聚乙烯醇缩丁醛，使其油漆干燥快，粘性好，涂刷在物体上可保持长时间不脱落。

A kind of paint

The present invention relates to a paint, which is characterized in that is composed of the following parts by weight of raw materials: paint component 30 50 copies, 20 copies of the 10 zeolite powder, rosin 8 13 copies, 20 copies, 15 titanium dioxide 5 polyvinyl butyral 10, no floating aluminium slurry 1 5 a 3 phosphoric acid 7, water 40 50 copies, 8 copies of 10 hydroxyethyl cellulose, talcum powder 4 6 copies, 2 copies of the 1 basic bismuth chloride, water soluble resin 2 4 copies, 7 copies of 5 butanol, butyl stearate 7 9 copies, 2 copies of 1 oil; the main raw material for some of the common market of the material, easy to obtain, and the cost is not high; the invention adds a phosphoric acid and polyvinyl butyral, the paint dry fast, good viscosity, brushing can keep long time off on an object.

【技术实现步骤摘要】
一种油漆
本专利技术涉及油漆领域，尤其涉及一种油漆。
技术介绍
油漆的一般成分包括：成膜物质，颜料、溶剂、助剂。油漆是一种能牢固覆盖在物体表面，起保护、装饰、标志和其他特殊用途的化学混合物涂料。中国涂料界比较权威的涂料工艺一书是这样定义的：涂料是一种材料，这种材料可以用不同的实施工艺涂覆在物件表面，形成粘附牢固、具有一定强度、连续固态薄膜。这样形成的膜通称涂膜，又称漆膜或涂层。属于有机化工高分子材料，所形成的涂膜属于高分子化合物类型。按照现代通行的化工产品的分类，涂料属于精细化工产品。现代的油漆的粉刷好以后不仅会传出一股刺鼻的味道，而且在一定的时间能不容易干，而且在粘性很差，经过风吹雨打后很容易脱落。
技术实现思路
本专利技术要解决的技术问题是提供一种粘性好，干燥快且适合任意环境中使用，在长时间不易脱落的油漆。为解决上述技术问题，本专利技术的技术方案为：一种油漆，其创新在于：由以下按照重量份的原料组成：油漆组分30-50份，沸石粉10-20份，松香树脂8-13份，钛白粉15-20份、聚乙烯醇缩丁醛5-10份，不浮型铝粉浆液1-5份，磷酸3-7份，水40-50份、羟乙基纤维素8-10份，滑本文档来自技高网...

【技术保护点】
一种油漆，其特征在于：由以下按照重量份的原料组成：油漆组分30‑50份，沸石粉10‑20份，松香树脂8‑13份，钛白粉15‑20份、聚乙烯醇缩丁醛5‑10份，不浮型铝粉浆液1‑5份，磷酸3‑7份，水40‑50份、羟乙基纤维素 8‑10 份，滑石粉 4‑6 份，碱式氯化铋 1‑2 份，水溶树脂 2‑4 份，丁醇 5‑7 份，硬脂酸丁酯 7‑9 份，石油 1‑2 份。

【技术特征摘要】
1.一种油漆，其特征在于：由以下按照重量份的原料组成：油漆组分30-50份，沸石粉10-20份，松香树脂8-13份，钛白粉15-20份、聚乙烯醇缩丁醛5-10份，不浮型铝...

【专利技术属性】
技术研发人员：唐正华，
申请(专利权)人：如皋市乐恒化工有限公司，
类型：发明
国别省市：江苏,32