本发明专利技术公开了一种装修装潢复合材料，由脲醛树脂、聚丙烯、相容剂、增韧剂、抗氧剂和细砂，其组分的重量份分别为脲醛树脂40‑50份，聚丙烯10‑20份，相容剂2‑3份，增韧剂8‑12份，抗氧剂0.5‑1.5份，细砂10‑15份。本发明专利技术的有益效果是：采用脲醛树脂与聚丙烯相结合的方式，能增强复合材料的粘结性，同时与其它原料相结合，相容性能好，牢固性能好，能低抗恶劣的环境，大大延长了使用寿命，性能稳定。

Composite material for decoration and decoration

The invention discloses a decoration composite material, composed of urea formaldehyde resin, polypropylene, compatibilizer, toughening agent, antioxidant and fine sand, the components of weight were 40 urea formaldehyde resin 50, PP 10 20 copies, 3 copies of 2 compatibilizer, toughener 8 12 0.5, antioxidant 1.5 copies, 15 copies of the 10 fine sand. The beneficial effect of the invention is that the urea formaldehyde resin and polypropylene combination, can enhance the adhesion of composite materials, combined with other raw materials, good compatibility, strong performance, low resistance to harsh environment, greatly prolong the service life, stable performance.

【技术实现步骤摘要】
一种装修装潢复合材料
本专利技术涉及一种复合材料，尤其涉及一种装修装潢复合材料。
技术介绍
一直以来，国内装修装潢业人士采用多种施工方案，不断地制造用各种材料，如：采用绷带用粘合剂裱上，铜带钉上火用柔性平底灰粘结，还有用环氧树脂合成材料施工，种种的办法和手段，都不能彻底解决各种材料的接缝问题，因填缝材料既要考虑各种材料的膨胀系数，又要考虑覆盖在各种装潢材料表面的施工装饰材料如涂料、墙体等，通常都达不到填缝的效果。因此，为解决上述问题，特提供一种新的技术方案。
技术实现思路
本专利技术提供一种装修装潢复合材料。本专利技术采用的技术方案是：一种装修装潢复合材料，由脲醛树脂、聚丙烯、相容剂、增韧剂、抗氧剂和细砂，其组分的重量份分别为脲醛树脂40-50份，聚丙烯10-20份，相容剂2-3份，增韧剂8-12份，抗氧剂0.5-1.5份，细砂10-15份。优选地，由脲醛树脂、聚丙烯、相容剂、增韧剂、抗氧剂和细砂，其组分的重量份分别为脲醛树脂48份，聚丙烯16.5份，相容剂2.8份，增韧剂10份，抗氧剂0.85份，细砂12份。优选地，所述增韧剂为乙烯-醋酸乙烯共聚物、聚烯烃弹性体或马来酸酐接枝。优选地，本文档来自技高网...

【技术保护点】
一种装修装潢复合材料，其特征在于：由脲醛树脂、聚丙烯、相容剂、增韧剂、抗氧剂和细砂，其组分的重量份分别为脲醛树脂40‑50份，聚丙烯10‑20份，相容剂2‑3份，增韧剂8‑12份，抗氧剂0.5‑1.5份，细砂10‑15份。

【技术特征摘要】
1.一种装修装潢复合材料，其特征在于：由脲醛树脂、聚丙烯、相容剂、增韧剂、抗氧剂和细砂，其组分的重量份分别为脲醛树脂40-50份，聚丙烯10-20份，相容剂2-3份，增韧剂8-12份，抗氧剂0.5-1.5份，细砂10-15份。2.根据权利要求1所述的一种装修装潢复合材料，其特征在于：由脲醛树脂、聚丙烯、相容剂、增韧剂、抗氧剂和细砂，其组分的重量份分别为脲醛树脂48份，聚丙烯16.5份，相...

【专利技术属性】
技术研发人员：郑国毜，
申请(专利权)人：太仓佩利斯高分子材料有限公司，
类型：发明
国别省市：江苏,32