本发明专利技术公开了一种纳米抗菌塑料瓶及其制备方法，抗菌塑料瓶原料包括聚烯烃50～70％、纳米抗菌剂2～10％、抗氧剂1～8％、润滑剂2～10％、助剂10～40％，所述纳米抗菌剂为纳米氧化锌、纳米二氧化钛和纳米二氧化硅，所述抗氧剂为四[β‑(3，5‑二叔丁基‑4‑羟基苯基)丙酸]季戊四醇酯，采用注射吹塑一步法完成抗菌塑料瓶，本发明专利技术提高抗菌瓶的抗压性、耐高温性\耐氧化性和长效性。

Nano antibacterial plastic bottle and preparation method thereof

The invention discloses a nano antibacterial plastic bottle and its preparation method and antibacterial plastic bottle materials including polyolefin 50 ~ 70%, 2 ~ 10% nano antibacterial agent, antioxidant 1 ~ 8%, 2 ~ 10%, lubricant additives 10 ~ 40%, the nano antibacterial agent of nanometer Zinc Oxide, nano titanium dioxide and nano silica, the four antioxidants [beta (3, 5 di-t-butyl 4 hydroxyphenyl) propionate pentaerythritol ester], complete antibacterial plastic bottles by one-step injection molding, improve the oxidation resistance and long-term antibacterial bottle compression resistance, high temperature resistance, the invention.

【技术实现步骤摘要】
一种纳米抗菌塑料瓶及其制备方法
本专利技术属于塑料加工成型领域，具体涉及一种纳米抗菌塑料瓶及其制备方法。
技术介绍
随着国民生活水平的提高,对塑料包装的要求也越来越高,对药品和食品等包装特别是药用及食用包装塑料瓶的卫生安全越来越引起广大消费者的密切关注,为此国家相关机关部门出台了一系列药用、食品用塑料瓶的安全措施，对大肠杆菌、金黄色葡萄球菌、霉菌等菌群数的作了严格的限制。但是该类包装物从生产、保存、运输、使用等经历较多环节,要使其符合国家相关卫生规定是很困难的事情。为此,亟待开发一种既具备良好抗菌性，又具备良好瓶口密封性纳米抗菌塑料瓶。目前研究开发的纳米抗菌塑料瓶在耐高温性、环保性、抗稳定性性能都存在一些不足，如中国专利CN104086851A公开了一种具有抗菌功能的聚乙烯塑料瓶及其制备方法，所述的抗菌母粒是含有无机纳米银抗菌剂的高密度聚乙烯树脂母粒，但其中所含纳米银对人体有害，无法用于药品及食品包装，中国专利CN104610657A公开了一种食品用抗菌塑料瓶，所述抑菌剂为聚赖氨酸或香精油，但这类有机抗菌剂的使用寿命短，且不耐高温，容易对药品和食品造成二次污染。专利
技术实现思路
为了弥补现本文档来自技高网...

【技术保护点】
一种纳米抗菌塑料瓶，其特征在于，包括如下质量百分比的原料：聚烯烃50～70％、纳米抗菌剂2～10％、抗氧剂1～8％、润滑剂2～10％、助剂10～40％，所述纳米抗菌剂为纳米氧化锌、纳米二氧化钛和纳米二氧化硅的一种或多种。

【技术特征摘要】
1.一种纳米抗菌塑料瓶，其特征在于，包括如下质量百分比的原料：聚烯烃50～70％、纳米抗菌剂2～10％、抗氧剂1～8％、润滑剂2～10％、助剂10～40％，所述纳米抗菌剂为纳米氧化锌、纳米二氧化钛和纳米二氧化硅的一种或多种。2.根据权利要1所述的纳米抗菌塑料瓶，其特征在于，包括如下质量百分比的原料：聚烯烃55％、纳米抗菌剂7％、抗氧剂5％、润滑剂3％、助剂22％。3.根据权利要1所述的纳米抗菌塑料瓶，其特征在于，所述聚烯烃为聚苯乙烯、聚乙烯和聚碳酸酯的一种或多种。4.根据权利要求1所述的纳米抗菌塑料瓶，其特征在于：所述抗氧剂为四[β-(3，5-二叔丁基-4-羟基苯基)丙酸]季戊四...