The present invention provides a halogen free low smoke high flame retardant fireproof cable material composition and its preparation method, which comprises the following components according to weight fraction: EVA resin: 20~40 parts; flame retardant: 20~32 parts; modified flame retardant: 30~50 parts; auxiliary agent: 0.5 to 3 parts. The preparation method is as follows: EVA resin, flame retardant additives and mixing, extrusion granulation, extrusion process, the temperature control of 8 temperature control areas were: 1 2 zone temperature is 100~120 C, 3 4 zone temperature is 120~140 C, 5 6 zone temperature is 130~150 C, 7 8 zone temperature is 140~160 DEG C. Compared with the prior art, the elongation at break of the cable material prepared by the invention is 170 - 220%, the tensile strength is 11 - 14MPa, and the oxygen index is 36~42.
【技术实现步骤摘要】
无卤低烟高阻燃型防火电缆料组合物及其制备方法
本专利技术涉及一种无卤低烟高阻燃型防火电缆料组合物及其制备方法，属于电缆制造材料
技术介绍
随着社会的进步和科学技术的飞速发展，PVC内在的弱点(燃烧时释放的大量烟雾，严重的腐蚀性气体和有毒气体)益专利技术显，低烟无卤作为一种不含有毒元素的材料得到广泛的应用。在地铁、高层建筑、商场、剧院、发电站、化学工厂、城市广场及其他公用事业等对电缆阻燃特性要求高的场合，都需要采用低烟无卤阻燃电缆。但是在现有技术中，低烟无卤电缆料普遍存在阻燃性较差、力学性能不强、抑烟效果较差等问题。
技术实现思路
针对现有技术中的缺陷，本专利技术的目的是提供一种无卤低烟高阻燃型防火电缆料组合物及其制备方法。本专利技术是通过以下技术方案实现的：第一方面，本专利技术提供了一种无卤低烟高阻燃型防火电缆料组合物，其包括按重量份数计的如下组分：若EVA树脂用量高于40份，会压缩添加剂份数，导致添加剂添加不足，产品性能不能达标；若EVA树脂用量低于20份，会导致塑化性能不足。阻燃剂用量高于32份，会导致与改性阻燃剂协同效果变差无法达到预期性能；若低于20...
【技术保护点】
一种无卤低烟高阻燃型防火电缆料组合物，其特征在于，包括按重量份数计的如下组分：
【技术特征摘要】
1.一种无卤低烟高阻燃型防火电缆料组合物，其特征在于，包括按重量份数计的如下组分：2.如权利要求1所述的无卤低烟高阻燃型防火电缆料组合物，其特征在于，所述阻燃剂包括：氢氧化铝和氢氧化镁中的一种或两种。3.如权利要求1所述的无卤低烟高阻燃型防火电缆料组合物，其特征在于，所述改性阻燃剂包括粒径为0.2～0.5um的氢氧化铝。4.如权利要求1所述的无卤低烟高阻燃型防火电缆料组合物，其特征...
【专利技术属性】
技术研发人员：陈建敏，李士兵，陈彬彬，
申请(专利权)人：上海欧伯尔塑胶有限公司，
类型：发明
国别省市：上海,31