The present invention provides a method for modifying surface of thermoplastic resin, the preparation method of the surface not only has low adsorption of proteins and cells, but also selective adsorption or adhesion of specific cells such as cancer cells, and also has excellent durability. A method for surface modification of thermoplastic resin made by hot objects, the method includes: Step 1, polymerization in the formation of objects on the surface; and step 2, the wavelength of 300 ~ 400nm UV irradiation from the polymerization of at least one point hydrophilic monomer free radical polymerization in which objects are formed on the surface of the grafted layer thickness is 2 ~ 100nm.
【技术实现步骤摘要】
表面改性方法
本专利技术涉及用于表面改性的方法，该方法制备的表面不仅表现出对来自血液或生物流体的蛋白质和细胞的低吸附性，而且还显示出对特定细胞如癌细胞的选择性吸附或粘附。本专利技术还涉及用于医疗和保健用途的基质，过滤器，通道，管和其它装置的表面改性体，其表面的至少一部分通过该方法改性。
技术介绍
用于医疗和保健用途或其他用途的基质(例如测试用基板，芯片，仪器)，过滤器，通道，管和其他装置具有缺陷，因为它们在使用时在身体内部或外部与血液或生物流体接触，血液或生物流体中的蛋白质和细胞可以粘附或吸附到装置的表面，从而损害装置的原始功能。为了捕获用于诊断或治疗的特定细胞如癌细胞，需要这些装置选择性地吸附和收集特定的细胞。然而，不幸的是，这些装置还难以选择性地吸附这些特定细胞。专利文献1提出用亲水性单体的聚合物涂覆用于医疗和保健用途的基质，过滤器，通道或管的表面，以解决上述问题。然而，该方法具有耐久性问题，因为涂层由于其亲水性而可能剥离或分离。引用列表专利文献1：JP2005-523981T。
技术实现思路
技术问题本专利技术的目的在于解决上述问题，提供用于表面改性热塑性树脂的...
【技术保护点】
一种用于表面改性由热塑性树脂制成的物体的方法，其特征在于，所述方法包括：步骤1：在所述物体的表面上形成聚合引发点；以及步骤2：通过用波长为300～400nm的紫外光照射，从所述聚合引发点使至少一种亲水性单体发生自由基聚合，以在所述物体的表面上形成厚度为2～100nm的接枝层。
【技术特征摘要】
2016.05.09 JP 2016-0939351.一种用于表面改性由热塑性树脂制成的物体的方法，其特征在于，所述方法包括：步骤1：在所述物体的表面上形成聚合引发点；以及步骤2：通过用波长为300～400nm的紫外光照射，从所述聚合引发点使至少一种亲水性单体发生自由基聚合，以在所述物体的表面上形成厚度为2～100nm的接枝层。2.一种用于表面改性由热塑性树脂制成的物体的方法，其特征在于，所述方法包括：步骤I：在光聚合引发剂的存在下，通过用波长为300-400nm的紫外光照射，使至少一种亲水性单体发生自由基聚合，以在所述物体的表面上形成厚度为2～100nm的接枝层。3.根据权利要求1所述的方法，其中，所述步骤1包括，将光聚合引发剂吸附到所述物体的表面，任选地随后用波长为300～400n...