Preparation method of composite hardfacing layer of the invention relates to a roller surfacing remelting combination, which is characterized in that the preparation method for the application of submerged arc welding or open arc surfacing welding way with surfacing material, welding method of welding roller surface, surfacing after a certain thickness, the plasma arc remelting of surfacing weld. The invention uses the high temperature of plasma arc, energy concentration, good stability, small deformation and has a hot surface, the surface grain refinement of roll, microstructure and the composition of surfacing layer uniform, internal S, number of P inclusions decreases, so as to realize the surface hardness and mechanical properties of roll evenly increased, reducing the probability of high the performance of roller after surface to produce white light fringe.
【技术实现步骤摘要】
轧辊表面堆焊重熔相结合的复合硬面层的制备方法
本专利技术涉及一种埋弧或明弧堆焊合金和等离子电弧重熔焊道相结合堆焊复合（再）制造轧辊表面的工艺，属于焊接
技术介绍
钢铁冶金行业是国家的基础行业，也是国家的重工业，其生产设备中的主要零备件——轧辊，大部分是在高交变应力、高热应力的恶劣环境下工作，如连铸辊、校直辊、支撑辊、助卷辊、夹送辊、工作辊等，导致轧辊过快报废。堆焊修复主要是采用适合的工艺和合适的堆焊材料将磨损的轧辊恢复到原始尺寸，研究发现，对轧辊表面进行堆焊处理，可以明显延长轧辊寿命，降低轧钢消耗。目前堆焊修复轧辊的方法主要有：埋弧堆焊，气体保护焊堆焊，自保护堆焊，等离子熔覆，激光熔敷，高能电子束焊，带极堆焊等。由于传统的埋弧堆焊，气体保护焊堆焊，自保护堆焊具有柱状晶粗大，合金成分偏析严重，组织不均匀，偶有夹渣等缺陷，严重限制了高性能轧辊的堆焊复合再制造应用。而新型的焊接如等离子熔覆堆焊，激光熔敷堆焊，电子束堆焊尽管其热量集中、保护气氛和可控性良好的等离子弧，填充材料主要为粉末状合金，堆焊过程稳定，堆焊层母材冲淡率低，成形平整、光滑，特别适用于堆焊钻基、...
【技术保护点】
一种轧辊表面堆焊重熔相结合的复合硬面层的制备方法，其特征在于：所述制备方法为应用埋弧堆焊或明弧堆焊方式配合堆焊材料、堆焊方法堆焊轧辊表面，堆焊一定厚度后，利用等离子弧对堆焊焊道进行重熔。
【技术特征摘要】
1.一种轧辊表面堆焊重熔相结合的复合硬面层的制备方法，其特征在于：所述制备方法为应用埋弧堆焊或明弧堆焊方式配合堆焊材料、堆焊方法堆焊轧辊表面，堆焊一定厚度后，利用等离子弧对堆焊焊道进行重熔。2.根据权利要求1所述的一种轧辊表面堆焊重熔相结合的复合硬面层的制备方法，其特征在于：1）重熔前堆焊材料的硬度比传统堆焊材料的硬度高3～8HRC；2）重熔前堆焊材料的合金成分比传统堆焊材料的合金成分高3～15%；3）杂质含量可适当提高，但不高于<0.04%；4）堆焊材料的碳含量不高于0.8%，常温断面伸长率不低于6%。3.根据权利要求1所述的一种轧辊表面堆焊重熔相结合的复合硬面层的制备方法，其特征在于：堆焊方法包括焊条电弧焊、熔化极气体保护电弧焊、钨极惰性气体保护焊、丝极埋弧焊及其组合。4.根据权利要求1所述的一种轧辊表面堆焊重熔相结合的复合硬面层...
【专利技术属性】
技术研发人员：顾晋南，朱龙华，王清宝，
申请(专利权)人：江阴中绿冶金设备有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。