The invention discloses a high quality relates to the technical field of casting sand, sand, sand, sand binder and the original auxiliary material mixing, the original sand is quartz sand; the sand binder for bentonite; the auxiliary material for pine nut shell powder; the pine nut shell powder according to the weight made from the following ingredients: 80, 70 pine nut shell 5 8 modified diatomite; the modified diatomite by urea and halloysite under alkaline conditions modified diatomite; a kind of high-quality sand prepared by the invention has excellent wet strength and stable gas quality, can enough to significantly improve the casting.
【技术实现步骤摘要】
一种优质型砂
本专利技术属于铸造型砂
，具体涉及一种优质型砂。
技术介绍
型砂一般由铸造用原砂、型砂粘结剂和辅加物等造型材料按一定的比例混合而成，也可用天然含粘土的硅砂，现有的型砂中通常采用煤粉来作为碳添加物来改善型砂的性能，但是，煤粉的添加，又会造成型砂溃散性差，含泥量、含水量较高，导致生产的铸件的表面光洁度不好，由型砂引起的废品率较高，型砂透气性较差，湿压强度低，稳定性较差。
技术实现思路
本专利技术的目的是针对现有的问题，提供了一种优质型砂。本专利技术是通过以下技术方案实现的：一种优质型砂，由原砂、型砂粘结剂和辅加物按100-105：5-8：0.5-0.8质量比例均匀混合制成；所述原砂为石英砂；所述型砂粘结剂为膨润土；所述辅加物为松子壳改性粉；所述松子壳改性粉按重量份计由以下成分制成：松子壳70-80、改性硅藻土5-8；所述改性硅藻土由尿素与埃洛石粉在碱性条件下改性处理硅藻土，其中尿素、埃洛石粉、硅藻土质量比例为1:3:20。进一步的，所述石英砂粒度为75目。进一步的，所述膨润土为钠基膨润土，钠基膨润土粒度为500目。进一步的，所述改性硅藻土制备方法为：将...
【技术保护点】
一种优质型砂，其特征在于，由原砂、型砂粘结剂和辅加物按100‑105：5‑8：0.5‑0.8质量比例均匀混合制成；所述原砂为石英砂；所述型砂粘结剂为膨润土；所述辅加物为松子壳改性粉；所述松子壳改性粉按重量份计由以下成分制成：松子壳70‑80、改性硅藻土5‑8；所述改性硅藻土由尿素与埃洛石粉在碱性条件下改性处理硅藻土，其中尿素、埃洛石粉、硅藻土质量比例为1:3:20。
【技术特征摘要】
1.一种优质型砂，其特征在于，由原砂、型砂粘结剂和辅加物按100-105：5-8：0.5-0.8质量比例均匀混合制成；所述原砂为石英砂；所述型砂粘结剂为膨润土；所述辅加物为松子壳改性粉；所述松子壳改性粉按重量份计由以下成分制成：松子壳70-80、改性硅藻土5-8；所述改性硅藻土由尿素与埃洛石粉在碱性条件下改性处理硅藻土，其中尿素、埃洛石粉、硅藻土质量比例为1:3:20。2.根据权利要求1所述的一种优质型砂，其特征在于，所述石英砂粒度为75目。3.根据权利要求1所述的一种优质型砂，其特征在于，所述膨润土为钠基膨润土，钠基膨润土粒度为500目。4.根据权利要求1所述的一种优质型砂，其特征在于，所述改性硅藻土制备方法为：将埃洛石粉与质量分数为5%的氢氧化钠溶液按2g：100ml的比例均匀混合到一起，加热至80℃，以500r/min转速搅拌2小时，然后再添加埃洛石粉质量三分之一的尿素，搅拌溶液后，得到埃洛石悬浊液，静置30min后，冷却至室温，然后添加尿素质量20倍的硅藻土，加热至50℃，置于功率为300W，频率为30...
【专利技术属性】
技术研发人员：孙爱琴，
申请(专利权)人：合肥市田源精铸有限公司，
类型：发明
国别省市：安徽,34