一种纳米复合光催化薄膜材料及其制备方法技术
Nano composite photocatalytic film material and preparation method thereof
The invention belongs to the field of photocatalysis, in particular relates to a photocatalytic film material and a preparation method thereof. In situ growth and ion exchange, BiOI and BiOBr with molar ratios of 0.1 to 0.5 form lamellar layered structure BiOI/BiOBr nanocomposite photocatalytic film materials. In the process of preparation, the BiOI/BiOBr material can be attached to the surface of stainless steel substrate by in-situ growth and ion exchange method to form a layer of film material with visible light catalytic activity. The preparation method of the invention is simple, easy to manipulate and low cost, and BiOI/BiOBr nano composite flake film structure with visible light catalytic effect is constructed, which has potential application prospect in the fields of water purification and marine antifouling.
【技术实现步骤摘要】
一种纳米复合光催化薄膜材料及其制备方法
本专利技术属于光催化领域，具体涉及一种光催化薄膜材料及其制备方法。
技术介绍
随着人类社会的全面进步，人类对原有自然界生态的影响越来越大，在过度开发利用自然资源时造就了一系列环境问题。其中水资源匮乏、水体污染等环境问题日益突出。因此污水治理就显得尤为重要。在众多的污水处理工艺中，光催化氧化降解技术，由于其具有高效、无选择性、稳定性高、绿色无毒、无二次污染、能耗低、操作简便和低成本等突出优点。特别是近年来以纳米TiO2为代表的半导体光催化材料被发现是一种很好的水处理光催化剂，它们可以在光照条件下产生电子-空穴对，部分电子、空穴可以迁移到半导体表面与水环境中的O2、OH-等反应生成化学氧化活性很强的自由基。这些自由基、光生电子和空穴可以直接与待降解反应物发生作用并将其氧化分解，达到光催化降解有机污染物的效果。BiOX(X＝Cl，Br，I)铋系化合物由于[Bi2O2]2+与卤素层之间较强的内建电场的存在，使得该类材料具有高的电子-空穴对分离效率，显现出较高的可见光催化活性。但是，受制于固有的能带结构，BiOX单体材料往往可见光催化...
【技术保护点】
一种纳米复合光催化剂薄膜材料，其特征在于：以原位生长法和离子交换的方式使摩尔比为0.1～0.5的BiOI和BiOBr形成片状层状结构的BiOI/BiOBr纳米复合光催化薄膜材料。
【技术特征摘要】
1.一种纳米复合光催化剂薄膜材料，其特征在于：以原位生长法和离子交换的方式使摩尔比为0.1～0.5的BiOI和BiOBr形成片状层状结构的BiOI/BiOBr纳米复合光催化薄膜材料。2.按权利要求1所述的纳米复合光催化剂薄膜材料的制备方法，其特征在于：1)将Bi(NO3)3·5H2O分散于过量的乙二醇中并加入PVP表面活性剂，随后加入与Bi(NO3)3·5H2O等摩尔量的KI水溶液，待两者混合均匀后转移至反应釜内衬中，然后将预处理好的待保护基体浸没于上述混合液，在120～160℃，反应4～12h，取出洗涤、干燥，待用；2)将四丁基溴化铵溶于过量的水中，待溶解后转移至反应釜内衬中，然后将上述干燥后基体浸没于反应釜内的混合液，在120～160℃，反应12～36h，即在基体表面形成片状...
【专利技术属性】
技术研发人员：王毅，龙洋，张盾，
申请(专利权)人：中国科学院海洋研究所，
类型：发明
国别省市：山东,37