一种轻质柔软隔音高粘附性壁纸及其制造方法技术

一种轻质柔软隔音高粘附性壁纸及其制备方法，包括以下步骤：(1)木浆纤维和醋酸丁酸纤维素打碎，混合均匀；(2)木浆纤维和醋酸丁酸纤维素混合物加入到水中，用打浆机进行打浆，制得混合浆料；(3)将混合浆经过抄纸、压榨、烘干、得到壁纸原纸；(4)将得到的壁纸原纸通过丙酮溶液，之后进行烘干，卷取工序制作轻质柔软隔音高粘附性的壁纸，该壁纸手感柔软，质地轻盈，并且与墙面粘附性好，使用时间长，同时具有较好的隔音效果。

Light, soft, sound insulation and high adhesion wallpaper and its manufacturing method

A light soft sound high adhesion wallpaper and preparation method thereof, comprising the following steps: (1) the wood pulp fiber and cellulose acetate butyrate break, mixed evenly; (2) adding water to the wood pulp fiber and cellulose acetate butyrate mixture, beating beater, prepared mixed slurry; (3) mixing the slurry after copy paper, pressing, drying, wallpaper base paper; (4) will be the base wallpaper by acetone solution, after drying, coiling process sound light soft high adhesion of the wallpaper, wallpaper soft, light texture and wall interference, good adhesion, long service time, and it has good sound effects.

【技术实现步骤摘要】
一种轻质柔软隔音高粘附性壁纸及其制造方法
本专利技术涉及建筑装饰材料，尤其涉及一种抗菌环保壁纸。
技术介绍
壁纸，即墙纸，是一种广泛用于室内装饰的材料，其可以由木浆纤维打浆后制成原纸，之后经过印花和后处理获得，也可以直接使用无纺布直接作为墙纸。壁纸因为其风格多变，色彩丰富，施工方便等因素，因此，深受大众欢迎。随着人类生活条件的改善，人们对日常使用的装饰材料的要求也越来越高，人们已经不仅仅要求壁纸具有普通的装饰性能，对壁纸的环保，抗菌性，阻燃性等一些列的附加性能有了更高的性能。目前我国许多家庭住房较为紧凑，而且在装修过程中，许多房间都是装修时进行隔断的，而这些后来砌成的墙面大都较薄，因此，容易造成房间与房间之间的隔音效果较差，进而影响到住户的隐私，因此很多家庭住户希望得到一种隔音的装饰材料。中国专利申请公开号为CN106592336A的专利技术专利，公开了一种隔音耐污墙纸及其制备方法，由以下重量份的组分制成：20-24份白胶香、23-25份松香、120-140份纸浆、10-16份防霉剂、10-14份防污剂、界面改性剂1-3份混合后，其中防菌剂由以下重量份的组分制成：石榴皮20-30份、本文档来自技高网...

【技术保护点】
一种轻质柔软隔音高粘附性壁纸，其特征在于，壁纸的原料包括木浆纤维30‑100份，醋酸丁酸纤维素5‑30份，丙酮100‑300份，水为其它原料总质量的20‑100倍，壁纸为多孔结构。

【技术特征摘要】
1.一种轻质柔软隔音高粘附性壁纸，其特征在于，壁纸的原料包括木浆纤维30-100份，醋酸丁酸纤维素5-30份，丙酮100-300份，水为其它原料总质量的20-100倍，壁纸为多孔结构。2.一种如权利要求1所述的抗轻质柔软隔音高粘附性壁纸，其特征在于，原料还包括涤纶纤维10-30份。3.一种如权利要求1所述的抗轻质柔软隔音高粘附性壁纸，其特征在于，原料中还包括阻燃剂、柔软剂、拒水剂中的一种或多种。4.一种如权利要求1所述的抗轻质柔软隔音高粘附性壁纸，其特征在于，原料中还包括交联剂。5.一种如权利要求1所述的轻质柔软隔音高粘附性壁纸，其特征在于，壁纸厚度小于0.5mm。6.一种如权利要求1-4任一项所述的轻质柔软隔音高粘附性壁纸的制备方法，其特征在于，包括以下步...

【专利技术属性】
技术研发人员：何洪学，
申请(专利权)人：武汉菡美洛建筑材料有限公司，
类型：发明
国别省市：湖北,42