一种测定铜的腐蚀失重的方法技术

本发明专利技术属于无机化学分析技术领域，具体地讲，本发明专利技术涉及一种测定铜的腐蚀失重的方法。首先称量待测样品的质量，然后在无氧条件下，将待检测样品置于除去氧气的氨水中，超声波震荡，待腐蚀产物全部溶解在氨水中后，对样品进行清洗，干燥，最后称量除去腐蚀产物后的样品的质量。待测样品的质量减去除去腐蚀产物后的样品的质量即为锈蚀铜片的腐蚀失重。

A method for determining corrosion weight loss of copper

The invention belongs to the field of inorganic chemical analysis technology, in particular, the invention relates to a method for measuring the corrosion weight loss of copper. The first weighing sample quality to be measured, then under anaerobic conditions, the test sample in the ammonia removal of oxygen, ultrasonic vibration, corrosion products to be dissolved in ammonia water after the samples were cleaned, dried, finally removing the corrosion products after weighing the quality of the sample. The quality of the sample to be measured minus the quality of the sample after removing the corrosion product is the corrosion weight loss of the corroded copper sheet.

【技术实现步骤摘要】
一种测定铜的腐蚀失重的方法
本专利技术属于无机化学分析
，具体地讲，本专利技术涉及一种测定铜的腐蚀失重的方法。
技术介绍
由于铜具有优良的延展性和导电、导热性，好的金属光泽，被广泛应用于电子电气工业、建筑工业、机械制造业、轻工业以及国防工业等领域。虽然铜的耐腐蚀性较强，但是在湿度较高时或在腐蚀性介质中，铜会发生较为严重的腐蚀，造成巨大的经济损失。因此，研究铜的腐蚀行为，具有很重要的意义。而研究铜的腐蚀行为，一般会通过腐蚀失重法来表示铜的腐蚀速度。所以，能准确测定铜的腐蚀失重对定量评估铜的腐蚀速率以及研究铜的腐蚀行为具有非常重要的意义。目前，测定铜的腐蚀失重的方法有：盐酸溶解法、氨基磺酸溶解法等。这两种方法都能比较好的将铜的腐蚀产物溶解下来，但是氨基磺酸溶解法在溶解铜的腐蚀产物时，形成的一价铜离子会发生歧化反应，生成的金属铜附着在铜片表面，使得去除腐蚀产物后的铜片的质量比实际质量大，最终导致测得的铜的腐蚀失重结果偏低。而盐酸溶解法是在有氧条件下进行，会稍微损害铜基体，将金属铜溶解下来，导致测得的铜的腐蚀失重结果偏高。进而急需一种能更准确测定铜的腐蚀失重的方法，来表示铜的腐蚀速度。本文档来自技高网...

【技术保护点】
一种测定铜的腐蚀失重的方法，其特征在于：在无氧条件下，将待处理样品置于除去氧气的氨水中，超声波震荡，使得待检测样品上的腐蚀产物溶解至氨水，而后将样品清洗、干燥，将震荡前后的待检测样品的质量差，即为待测样品的腐蚀失重。

【技术特征摘要】
1.一种测定铜的腐蚀失重的方法，其特征在于：在无氧条件下，将待处理样品置于除去氧气的氨水中，超声波震荡，使得待检测样品上的腐蚀产物溶解至氨水，而后将样品清洗、干燥，将震荡前后的待检测样品的质量差，即为待测样品的腐蚀失重。2.按权利要求1所述的测定铜的腐蚀失重的方法，其特征在于：所述氨水浓度(与水体积比)为1:10-1:3。3.按权利要求1所述测试锈蚀铜片腐蚀失重的方法，其特征在于：1)在无氧条件下，将待测样品浸入除去氧气的氨水中中，经震荡将待处理铜片样...

【专利技术属性】
技术研发人员：陈卓元，李坤，
申请(专利权)人：中国科学院海洋研究所，
类型：发明
国别省市：山东,37