The invention of the cement tile made of cement, sand, gravel, pigment, composite agent according to the proportion and the amount of processing is made. The compound is composed of polyvinyl alcohol aqueous solution of A component and trimeric methanol resin of B component. The material is mixed and stirred so as to form a state of flow rather than flow, which is loaded into the tile mould and is released after solidification. For water conservation, the formation of the cement tile. Due to the processing methods of typical cement components, make the production process more simple color. To reduce the process of building and roasting, can save fuel and reduce environmental pollution.
【技术实现步骤摘要】
一种水泥彩瓦及其制造方法
本专利技术涉及一种建筑构件，特别是一种以水泥、沙子和色料为主要原料制成的不用烧制的彩瓦。本专利技术还涉及上述彩瓦的制造方法。
技术介绍
传统建筑物使用屋面材料是由泥土烧制的泥制瓦，由于其颜色单一、工艺复杂，且在制作时必须破坏宝贵的土地资源等问题将逐渐被淘汰。由于我国具有特殊喜爱瓦制屋面的传统，因此就必须开发出相应的替代产品来弥补上述泥制瓦淘汰的空白。琉璃瓦虽然美观实用，但因其需建窑并进行高温焙烧，造成工艺复杂，不仅需使用燃料焙烧，成本较高，而且会带来严重的污染问题。
技术实现思路
本专利技术的目的在于提供一种水泥彩瓦，具有生产成本低廉、工艺设备简单、避免土地资源浪费的优点，并且可以不用烧制，具有多种色彩。本专利技术的水泥彩瓦由水泥、沙子、石子、色料、复合剂和适量水加工制成。按重量计，各种原料的用量为：水泥：1000～1600份；沙子：3000～4000份；石子：20～300份；色料：20～50份；复合剂：25～35份。上述的该色料可以是红色的氧化铁红、绿色的氧化铁绿、蓝色的氧化铁篮或它们的混合物其中之一，以形成颜色。上述的该复合剂可以包括A组...
【技术保护点】
一种水泥彩瓦，由水泥、沙子、石子、色料、复合剂和水 制成，其特征在于：按重量计，各种原料的用量为： 水泥：1000～1600份； 沙子：3000～4000份； 石子：20～300份； 色料：20～50份； 复合剂：25～35份； 所述的色料是红色的氧化铁红、绿色的氧化铁绿、蓝色的氧 化铁篮或它们的混合物其中之一； 所述的复合剂包括A组分的聚乙烯醇水溶液和B组分的三聚 氢胺甲醇树脂，其使用比例为A∶B＝1∶2。
【技术特征摘要】
1.一种水泥彩瓦，由水泥、沙子、石子、色料、复合剂和水制成，其特征在于：按重量计，各种原料的用量为：水泥：1000～1600份；沙子：3000～4000份；石子：20～300份；色料：20～50份；复合剂：25～35份；所述的色料是红色的氧化铁红、绿色的氧化铁绿、蓝色的氧化铁篮或它们的混合物其中之一；所述的复合剂包括A组分的聚乙烯醇水溶液和B组分的三聚氢胺甲醇树脂，其使用比例为A∶B＝1∶2。2.根据权利要求1所述的水泥彩瓦，其特征在于：该A组分的溶液是在1000份70摄氏度的水内加入20～40份的聚乙烯醇，边加入边升温到9...