The invention discloses a method for cutting adhesive, which comprises epoxy resin, curing agent, diluent, three methyl phenol and three oxidation of three aluminum powder, the hardening agent is ethylene diamine, the diluent is two butyl are described for each component of the multi wire cutting glue the weight number of copies were: the epoxy resin accounted for 100 of 120 copies, the ethylenediamine accounted for 10 20 copies, the two butyl accounted for 5 in 10, the three methyl phenol accounted for 10 in 30, three of the three aluminum oxide accounts for 5 20. By the way, the invention is used for cutting the adhesive composition and proportion, by setting reasonable, the product shrinkage rate is small, the linear expansion coefficient is small, good dimensional stability of adhesive, heat resistance good water resistance.
【技术实现步骤摘要】
一种用于多线切割的粘接胶
本专利技术涉及粘接胶领域，特别是涉及一种用于多线切割的粘接胶。
技术介绍
环氧树脂胶广泛适用于光电、太阳能单晶硅、多晶硅、半导体等的切割和研磨加工，为光伏行业硅棒切割而应用的产品，使用于铁板基座和玻璃，人工和自动化粘结过程，环氧胶可以粘接、灌封、密封、绝缘等等，应用范围广泛，现有的环氧胶大多数粘接力小，抗开裂、抗冲击性能差。
技术实现思路
本专利技术主要解决的技术问题是提供一种用于多线切割的粘接胶，通过设置合理的成分和比例，获得的产品收缩率小，线胀系数也很小，胶层的尺寸稳定性好，耐热耐水性能好。为解决上述技术问题，本专利技术采用的一个技术方案是：提供一种用于多线切割的粘接胶，包括：环氧树脂、硬化剂、稀释剂、三甲基苯酚和三氧化三铝粉，所述的硬化剂是乙二胺，所述的稀释剂是二丁酯，所述的用于多线切割的粘接胶中各成分所占重量份数分别为：所述的环氧树脂占100-120份，所述的乙二胺占10-20份，所述的二丁酯占5-10份，所述的三甲基苯酚占10-30份，所述的三氧化三铝粉占5-20份。在本专利技术一个较佳实施例中，所述的环氧树脂占105份。在本专利技...
【技术保护点】
一种用于多线切割的粘接胶，其特征在于，包括：环氧树脂、硬化剂、稀释剂、三甲基苯酚和三氧化三铝粉，所述的硬化剂是乙二胺，所述的稀释剂是二丁酯，所述的用于多线切割的粘接胶中各成分所占重量份数分别为：所述的环氧树脂占100‑120份，所述的乙二胺占10‑20份，所述的二丁酯占5‑10份，所述的三甲基苯酚占10‑30份，所述的三氧化三铝粉占5‑20份。
【技术特征摘要】
1.一种用于多线切割的粘接胶，其特征在于，包括：环氧树脂、硬化剂、稀释剂、三甲基苯酚和三氧化三铝粉，所述的硬化剂是乙二胺，所述的稀释剂是二丁酯，所述的用于多线切割的粘接胶中各成分所占重量份数分别为：所述的环氧树脂占100-120份，所述的乙二胺占10-20份，所述的二丁酯占5-10份，所述的三甲基苯酚占10-30份，所述的三氧化三铝粉占5-20份。2.根据权利要求1所述的用于多...