The invention discloses a preparation method of a low odor plastic masterbatch, which comprises the following steps: (1) four Butyl Ammonium fluoride, ethylenediamine propyl sulfonate, anise alcohol, cinnamic acid methyl benzene mixture, using 500r/min speed continuous stirring for 120 150min, prepared plastic deodorant (2;) the polyvinyl chloride resin, glue incense, talcum powder, coupling agent, antioxidant, plastic deodorant high-speed mixing, plastic extrusion granulation extruder, plastic masterbatch prepared low odor. Method of preparing low odor plastic masterbatch provided by the invention has the advantages of simple operation, low cost, PVC plastic masterbatch prepared, almost no smell, solves the technical problems of PVC material in the prior art heavy smell.
【技术实现步骤摘要】
一种低气味塑料母粒的制备方法
本专利技术属于塑料母粒的制备
，具体涉及一种低气味塑料母粒的制备方法。
技术介绍
聚氯乙烯，是氯乙烯单体在过氧化物、偶氮化合物等引发剂，或在光、热作用下按自由基聚合反应机理聚合而成的聚合物。氯乙烯均聚物和氯乙烯共聚物统称之为氯乙烯树脂。PVC曾是世界上产量最大的通用塑料，应用非常广泛。在建筑材料、工业制品、日用品、地板革、地板砖、人造革、管材、电线电缆、包装膜、瓶、发泡材料、密封材料、纤维等方面均有广泛应用。但是聚氯乙烯在使用的过程中，易挥发出氯化氢或者一些难闻的有机气体，严重影响了聚氯乙烯制品的品质。
技术实现思路
为了解决上述技术问题，本专利技术提供一种低气味塑料母粒的制备方法。本专利技术是通过以下技术方案实现的。一种低气味塑料母粒的制备方法，包括以下操作步骤：（1）按重量份计，将50-70份四丁基氟化铵、10-14份乙二胺基丙磺酸钠、1-2份茴香醇、4-6份肉桂酸苯甲酯混合后，采用500r/min的转速持续搅拌120-150min后，制得塑料除味剂；（2）按重量份计，将50-70份聚氯乙烯树脂、2-4份白胶香、10-14份滑石...
【技术保护点】
一种低气味塑料母粒的制备方法，其特征在于，包括以下操作步骤：（1）按重量份计，将50‑70份四丁基氟化铵、10‑14份乙二胺基丙磺酸钠、1‑2份茴香醇、4‑6份肉桂酸苯甲酯混合后，采用500r/min的转速持续搅拌120‑150min后，制得塑料除味剂；（2）按重量份计，将50‑70份聚氯乙烯树脂、2‑4份白胶香、10‑14份滑石粉、4‑7份偶联剂、1‑2份抗氧剂、5‑8份塑料除味剂高速混合均匀后，采用塑料挤出机挤出造粒，制得低气味塑料母粒。
【技术特征摘要】
1.一种低气味塑料母粒的制备方法，其特征在于，包括以下操作步骤：（1）按重量份计，将50-70份四丁基氟化铵、10-14份乙二胺基丙磺酸钠、1-2份茴香醇、4-6份肉桂酸苯甲酯混合后，采用500r/min的转速持续搅拌120-150min后，制得塑料除味剂；（2）按重量份计，将50-70份聚氯乙烯树脂、2-4份白胶香、10-14份滑石粉、4-7份偶联剂、1-2份抗氧剂、5-8份塑料除味剂高速混合均匀后，采用塑料挤出机挤出造粒，制得低气...
【专利技术属性】
技术研发人员：王雪，
申请(专利权)人：阜南县鲲鹏塑业科技有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。