The invention provides a nano fresh-keeping plastic film, made from the following raw materials in weight portion: 20, 10 nano titanium dioxide nano graphene 5 15 copies, 12 copies of the 8 nanometer silver powder, linear low density polyethylene 20 50 copies, 65 copies, 30 polyethylene resin, silane coupling agent 6 12 two copies, 8 copies, 3 octyl ethoxylated alkyl amine 6 15 copies, 10 copies, 5 glycerol ester of ultraviolet absorbent 3 8. By adding silver nanoparticles with ethylene oxide effect, nano plastic film can make the ethylene gas release accelerated oxidation of fruits and vegetables and other foods, in order to reduce the ethylene content of packaging in the internal environment, achieve good preservation effect.
【技术实现步骤摘要】
一种纳米保鲜塑料薄膜
本专利技术属于塑料制品
,具体涉及一种纳米保鲜塑料薄膜。
技术介绍
食品包装作为目前包装领域所占份额较重的一部分,在整个包装领域中占有重要的地位。近些年在食品安全领域出现的各种问题,使人们更加注重对食品及其包装材料,甚至整个生产工艺、包装过程的安全性,这使得对食品包装材料的探究提上日程。塑料因其质量轻、使用方便、价格低等特点而被广泛应用于食品包装中。果蔬等新鲜食品在储存时会释放出乙烯气体,而乙烯积累到一定浓度时就会加速食品腐烂,因此,如何减少塑料包装材料中的乙烯含量是急需解决的问题。
技术实现思路
为解决上述问题,本专利技术的目的在于,具体的技术方案为:一种纳米保鲜塑料薄膜,由以下重量份的原料制成:纳米二氧化钛10-20份、纳米石墨烯5-15份、纳米银粉末8-12份、线性低密度聚乙烯20-50份、聚乙烯树脂30-65份、硅烷偶联剂6-12份、二辛酯3-8份、乙氧基化烷基胺6-15份、甘油酯5-10份、紫外线吸收剂3-8份。进一步的,本专利技术所述的一种纳米保鲜塑料薄膜,由以下重量份的原料制成:纳米二氧化钛15份、纳米石墨烯10份、纳米银粉末10份、线性低密度聚乙烯30份、聚乙烯树脂45份、硅烷偶联剂10份、二辛酯5份、乙氧基化烷基胺12份、甘油酯8份、紫外线吸收剂5份。进一步的,所述纳米银粉末的粒径为18-40nm。进一步的,所述紫外线吸收剂为邻羟基苯甲酸苯酯、2-(2-羟基-3-特丁基-5-甲基苯基)-5-氯苯并三唑或2-(2’-羟基-3’,5’-二叔苯基)-5-氯化苯并三唑的一种。进一步的,所述纳米保鲜塑料薄膜的厚度为0.008 ...
【技术保护点】
一种纳米保鲜塑料薄膜,其特征在于,由以下重量份的原料制成:纳米二氧化钛10‑20份、纳米石墨烯5‑15份、纳米银粉末8‑12份、线性低密度聚乙烯20‑50份、聚乙烯树脂30‑65份、硅烷偶联剂6‑12份、二辛酯3‑8份、乙氧基化烷基胺6‑15份、甘油酯5‑10份、紫外线吸收剂3‑8份。
【技术特征摘要】
1.一种纳米保鲜塑料薄膜,其特征在于,由以下重量份的原料制成:纳米二氧化钛10-20份、纳米石墨烯5-15份、纳米银粉末8-12份、线性低密度聚乙烯20-50份、聚乙烯树脂30-65份、硅烷偶联剂6-12份、二辛酯3-8份、乙氧基化烷基胺6-15份、甘油酯5-10份、紫外线吸收剂3-8份。2.根据权利要求1所述的一种纳米保鲜塑料薄膜,其特征在于,由以下重量份的原料制成:纳米二氧化钛15份、纳米石墨烯10份、纳米银粉末10份、线性低密度聚乙烯30份、聚乙烯树脂45份、硅烷偶联剂10份、二...