The invention discloses a diatom clay board, which is made up of 5~35 pieces of diatom minerals, 65~95 clay parts and 0~10 tourmaline parts according to the weight portion. The invention also discloses the preparation method of the diatom clay plate, which mixes the raw material and the water to form the required clay plate shape, and obtains the diatomite clay plate by drying and calcining. Compared with the traditional clay board products, the invention has the advantages of light weight, good moisture absorption, good heat insulation performance and clean air, and is suitable for the use of indoor wall in the room, so as to make up for the deficiency of the traditional clay board in interior decoration.
【技术实现步骤摘要】
一种硅藻陶土板及其制备方法和应用
本专利技术涉及建筑内墙用饰面陶土板
更具体地，涉及一种硅藻陶土板及其制备方法和应用。
技术介绍
居室装饰是一个广泛存在于我们身边的需求，尤其是人们在对舒适生活追求的同时，也会注重装饰美带给我们的享受。内墙面装饰材料除了涂料、墙纸，就是木材，传统材料应用广泛但也有不足，比如墙纸及涂料除了耐久性差以外，用的不好还会带来一定程度的污染，危害环境。目前传统的普通陶土板都是按照外墙标准制作的，因此，实际应用也都是使用在外墙墙面。因此，需要提供一种新型质轻、且保温及防潮性好、可以用做内墙环保装饰材料的硅藻陶土板。
技术实现思路
本专利技术的一个目的在于提供一种硅藻陶土板。本专利技术的另一个目的在于提供一种硅藻陶土板的制备方法。本专利技术的第三个目的在于提供一种硅藻陶土板的应用。为达到上述第一个目的，本专利技术采用下述技术方案：一种硅藻陶土板，按重量份数计，包括硅藻矿物质5～35份、陶土65～95份、电气石0～10份。本专利技术的硅藻陶土板不但装饰效果好同时还具有诸多优点，添加了硅藻矿物质等多孔材料，从而减轻重量、同时还有良好的透气性及保温...
【技术保护点】
一种硅藻陶土板，其特征在于，按重量份数计，所述硅藻陶土板包括硅藻矿物质5～35份、陶土65～95份、电气石0～10份。
【技术特征摘要】
1.一种硅藻陶土板，其特征在于，按重量份数计，所述硅藻陶土板包括硅藻矿物质5～35份、陶土65～95份、电气石0～10份。2.根据权利要求1所述的硅藻陶土板，其特征在于，所述硅藻矿物质为硅藻土和/或硅藻页岩粉。3.根据权利要求1或2所述的硅藻陶土板，其特征在于，按照质量百分数计，所述陶土包括粘土48-51wt％、高岭土10-12wt％、钾长石18-20wt％、锂长石7-9wt％、硅辉石2.5-3.5wt％、滑石2.5-3.5wt％、胚体增强剂3.2-3.3wt％、腐钠0.2-0.3wt％和解胶剂0.3-0.4wt％。4.如权利要求1～3任一所述的硅藻陶土板的制备方法，其特征在于，包括如下步骤：将原料与水混合后得到湿胚，将湿胚制成所需陶土板形状，干燥煅烧制得硅藻陶土板。5.根据权利要求4所述的制备方法，其特征在于，所述湿胚的含水量为14wt％～16wt％。6.根据权利要求4所述的制备方法，其特征在于，所述煅烧温度为950～1...
【专利技术属性】
技术研发人员：郑爱民，李国权，樊万科，郑宏宇，李志辉，
申请(专利权)人：北京大督硅藻新材料技术股份有限公司，
类型：发明
国别省市：北京,11
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。