Anti oxidation treatment process for automobile parts provided by the invention, including mechanical polishing, alkali cleaning, pickling, washing, drying and coating steps, using the polishing device to polished samples were mechanically polished by alkali washing and pickling to remove surface contaminants, a passivation layer is formed, and then washed with water and dried, finally. The coating is formed. The present invention before plating coating was first a series of treatment process of automobile parts surface, good adhesion and coating, prolong the service life of auto parts, auto parts to ensure no rust, energy saving and environmental protection.
【技术实现步骤摘要】
一种汽车零部件的防氧化处理工艺
本专利技术涉及机械加工用具制造
，特别是涉及一种汽车零部件的防氧化处理工艺。
技术介绍
汽车零部件作为汽车工业的基础，是支撑汽车工业持续健康发展的必要因素。特别是当前汽车行业正在轰轰烈烈、如火如荼开展的自主开发与创新，更需要一个强大的零部件体系作支撑。当前在许多先进技术部门中，需使用高熔点的金属材料制造特殊用途的零件，但这些零件在高温腐蚀性介质中容易氧化而损坏，例如，转子发动机的内腔、电子管及晶体管的管脚与插座等，常需要镀镍、铬和铬合金镀层。在某些情况下，还使用复合镀层，如Ni-ZrO2、Ni-Al2O3、Cr-TiO2、Cr-ZrB等，以及Fe、Ni、Cr扩散镀层。镀(如电镀)在金属底子上面的极薄的通常为贵金属的表层；装饰性或保护性的外部镀层；为了好看或储藏而涂在某些物品上的一层稀薄的金属或为仿造某种贵重金属，在普通金属的表面镀上这种贵重金属的薄层。一般在工业上镀层的用途就是保护作用，比如：镀金的它的防氧化能力就很强，还有防潮湿、接触性能、防盐雾等等性能就会加强。防氧化剂是一类照相化学药品，本身系一弱还原剂，加在照相乳剂或显...
【技术保护点】
一种汽车零部件的防氧化处理工艺，其特征在于，包括机械抛光、碱洗、酸洗、水洗、干燥和镀层等步骤，具体工艺步骤如下：(1)机械抛光：利用抛光装置对汽车零部件表面进行机械抛光，形成抛光层；(2)碱洗：对上述抛光层采用碱性溶液的清洗；(3)酸洗：再采用酸性的缓冲剂去除抛光层表面的残留物层,在去除残留物层之后，形成覆盖抛光层的钝化层；(4)水洗：通过喷嘴喷淋超纯水清洗抛光层；(5)干燥：对水洗后的抛光层进行干燥处理；(6)镀层：并依次在其表面依次为塑料层、氧化铝层、防腐蚀层，再通过热熔方式去掉防腐蚀层表面的凸起。
【技术特征摘要】
1.一种汽车零部件的防氧化处理工艺，其特征在于，包括机械抛光、碱洗、酸洗、水洗、干燥和镀层等步骤，具体工艺步骤如下：(1)机械抛光：利用抛光装置对汽车零部件表面进行机械抛光，形成抛光层；(2)碱洗：对上述抛光层采用碱性溶液的清洗；(3)酸洗：再采用酸性的缓冲剂去除抛光层表面的残留物层,在去除残留物层之后，形成覆盖抛光层的钝化层；(4)水洗：通过喷嘴喷淋超纯水清洗抛光层；(5)干燥：对水洗后的抛光层进行干燥处理；(6)镀层：并依次在其表面依次为塑料层、氧化铝层、防腐蚀层，再通过热熔方式去掉防腐蚀层表面的凸起。2.根据权利要求1所述的汽车零部件的防氧化处理工艺，其特征在于，所述步骤(2)和(3)中碱洗和酸洗试剂的pH值通过硫酸、盐酸、硝酸、磷酸、氢...
【专利技术属性】
技术研发人员：洪浩伟，
申请(专利权)人：安徽凯密克企业管理咨询有限公司，
类型：发明
国别省市：安徽,34