A kind of PC/ABS resistant alloy materials of automotive antifreeze, consists of the following parts by weight of material: PC resin 38 ~ 72, 23 ~ 58 ABS resin and PPA resin 4 ~ 12, 1 ~ 3, the compatibilizer of antioxidant 0.1 ~ 1, 0.1 ~ 1 lubricant. The preparation method includes: step a, mixing PC resin, ABS resin, PPA resin, compatibilizer, antioxidant and lubricant evenly; step B, extruding the mixture obtained in step a, and then mixing and granulating. The alloy material has excellent corrosion resistance to automobile antifreeze liquid, and it has little appearance change after contact with automobile antifreeze liquid, and it will not affect the safety. The preparation method is simple and easy to be produced.
【技术实现步骤摘要】
一种耐汽车防冻液的PC/ABS合金材料及其制备方法
本专利技术涉及高分子材料成型加工领域，尤其涉及一种耐汽车防冻液的PC/ABS合金材料及其制备方法。
技术介绍
PC/ABS合金材料兼顾了PC和ABS二者的优点，具有优良的力学性能和加工性能，在汽车、电子、通讯和化工等领域有着广泛的应用。尤其是近年来汽车消费市场日益火爆，汽车以塑代钢的轻量化趋势下，使PC/ABS合金材料在汽车领域的用量迅猛上升。但是，汽车制件由于经常接触化学物质，例如玻璃水、汽车防冻液等，所以，要求汽车制件具有对这些化学物质耐腐蚀的性能。但是PC/ABS合金材料本身对汽车防冻液的耐受性很差，与汽车防冻液接触后，其表面就会受到腐蚀，外观发生变化，严重影响视觉美观，甚至变形会影响安全性。因此，研究如何提高PC/ABS合金材料对汽车防冻液的耐腐蚀性具有现实而重要的意义。
技术实现思路
本专利技术的目的在于提出一种耐汽车防冻液腐蚀的PC/ABS改性材料。一种耐汽车防冻液的PC/ABS合金材料，由以下重量份的物质组成：PC树脂38～72份、ABS树脂23～58份、PPA树脂4～12份、相容剂1～3份、抗氧剂0....
【技术保护点】
一种耐汽车防冻液的PC/ABS合金材料，其特征在于，由以下重量份的物质组成：PC树脂38～72份、ABS树脂23～58份、PPA树脂4～12份、相容剂1～3份、抗氧剂0.1～1份、润滑剂0.1～1份。
【技术特征摘要】
1.一种耐汽车防冻液的PC/ABS合金材料，其特征在于，由以下重量份的物质组成：PC树脂38～72份、ABS树脂23～58份、PPA树脂4～12份、相容剂1～3份、抗氧剂0.1～1份、润滑剂0.1～1份。2.如权利要求1所述的耐汽车防冻液的PC/ABS合金材料，其特征在于：所述PC树脂的分子量为17000～30000g/mol，玻璃化温度为140～150℃。3.如权利要求1所述的耐汽车防冻液的PC/ABS合金材料，其特征在于：所述ABS树脂中丁二烯含量为10～55wt％。4.如权利要求1所述的耐汽车防冻液的PC/ABS合金材料，其特征在于：所述相容剂为AS-g-GMA共聚物。5.如权利要求4所述的耐汽车防冻液的PC/ABS合金材料，其特征在于：所述AS-g-GMA共聚物中的GMA的含量为5～8wt％。6.如权利要求1所述的耐汽车防冻液的PC/ABS合金材料，其特征在于，所述抗氧剂为二缩三乙二醇双[β-(3-叔丁基-4-...
【专利技术属性】
技术研发人员：周中玉，辛敏强，郭东平，李军宏，
申请(专利权)人：广东锦湖日丽高分子材料有限公司，
类型：发明
国别省市：广东,44