A FEP insulation material has excellent performance and manufacturing method of anti aging, which belongs to the technical field of new materials, 75 ~ 85% O2 less than 30ppm chromatographic peak of tetrafluoroethylene monomer, 15 to 25% purity more than 99.999% fluorine six propylene, initiator 5 ~ 4.7% 7% active oxygen content is higher than the level of ultra pure water after polymerization. Ingredients, polymerization, polymer condensation, crushing and drying of FEP material. The material ingredients of science, advanced technology, manufacturing products of good quality and can be used as high performance wire insulation materials, molding materials, semiconductor industry, insulation anti-corrosion materials, large-scale petrochemical enterprises heavy anti-corrosion materials, sealing materials and the solar industry's high performance thin film materials, widely used, the effect is very good.
【技术实现步骤摘要】
一种绝缘抗老化性能优异的FEP材料及其制造方法
本专利技术属于新材料
，涉及一种FEP材料及其制造方法，特别是涉及一种绝缘抗老化性能优异的FEP材料及其制造方法。
技术介绍
目前市场上的FEP材料不引燃，可阻止火焰的扩散。它具有优良的耐候性，摩擦系数较低，从低温到392F均可使用。FEP材料可制成用于挤塑和模塑的粒状产品，用作流化床和静电涂饰的粉末，也可制成水分散液。半成品有膜、板。棒和单纤维。美国市场经销的FEP有DUIPont公司的Teflon牌、Daikin公司的Neoflo牌、HoechstCelanese公司的IHoustaflow牌。其主要的用途是用于制作管和化学设备的内衬、滚筒的面层及各种电线和电缆，如飞机挂钩线、增压电缆、报警电缆、扁形电缆和油井测井电缆。FEP膜已见用作太阳能收集器的薄涂层。随着现代化建设进程的加快，航空、石化、半导体、太阳能等产业的迅速发展，各行各业对高性能氟材料FEP的需求越来越大，要求越来越高，而现有的FEP材料已不能满足市场的需要和要求，研究出一种高性能氟材料是科研单位和生产企业的一项迫切任务。
技术实现思路
本专利技术...
【技术保护点】
一种绝缘抗老化性能优异的FEP材料，其特征在于，包括如下重量百分比组份：色谱单峰O2≤30ppm的四氟乙烯单体75～85%、纯度≥99.99%的六氟丙烯15～25%、活性氧含量≥4.7%的引发剂5～7%，其余为聚合级超纯水。
【技术特征摘要】
1.一种绝缘抗老化性能优异的FEP材料，其特征在于，包括如下重量百分比组份：色谱单峰O2≤30ppm的四氟乙烯单体75～85%、纯度≥99.99%的六氟丙烯15～25%、活性氧含量≥4.7%的引发剂5～7%，其余为聚合级超纯水。2.如权利要求1所述的一种绝缘抗老化性能优异的FEP材料的制造方法，其特征在于，包括如下步骤：(1)将75～85%色谱单峰O2≤30ppm的四氟乙烯单体C2F4和30～40%纯度≥99.99%的六氟丙烯C3F6用隔膜泵混和均匀成初始单体，打入初始槽；(2)先将聚合釜清洗干净、氮气真空排氧，O2≤30ppm，夹套内通入冷媒介质保冷，然后加入部分聚合级超纯水进行搅拌，用隔膜泵从初始槽向聚合釜内压入初始单体...
【专利技术属性】
技术研发人员：糜万俊，
申请(专利权)人：江苏华奥高科技发展有限公司，
类型：发明
国别省市：江苏,32